Comparative study of β-Si_3N_4 powders prepared by SHS sintered by spark plasma sintering and hot pressing

在线全文

学校读者我要写书评

暂无评论

Journal of University of Science and Technology Beijing 2007年第3期14卷 271-275页

作者： Ling Bai Xiaodong Mao Weiping Shen Changchun Ge Laboratory of Special Ceramics and Powder Metallurgy University of Science and Technology Beijing Beijing 100083 China

β-Si3N4 powders prepared by self-propagating high-temperature synthesis （SHS） with additions of Y2O3 and Al2O3 were sintered by spark plasma sintering （SPS）. The densification, microstructure, and mechanical properties of Si3N4 ceramics prepared using this method were compared with those obtained by hot pressing process. Well densified Si3N4 ceramics with finer and homogeneous microstructure and better mechanical properties were obtained in the case of the SPS technique at 200°C lower than that of hot pressing. The microhardness is 15.72 GPa, the bending strength is 716.46 MPa, and the fracture toughness is 7.03 MPa·m1/2.

关键词： self-propagating high-temperature synthesis (SHS) hot pressing spark plasma sintering (SPS) silicon nitride mechanicalproperties

Diffusion behavior of Nb element in high Nb containing TiAl Alloys by reactive hot pressing

在线全文

学校读者我要写书评

暂无评论

Rare Metals 2006年第4期25卷 349-354页

作者： WANG Yanhang LIN Junpin HE Yuehui WANG Yanli CHEN Guoliang State Key Laboratory for Advanced Metals and Materials University of Science and Technology Beijing Beijing 100083 China State Key Laboratory for Powder Metallurgy Central South University Changsha 410083 China

Diffusion behavior of Nb in elemental powder metallurgy high Nb containing TiAl alloys was investigated. The results show that Nb element dissolves into the matrix by diffusion. Pore nests are formed in situ after Nb diffusion. With the increase in hot pressing temperature, the diffusion of Nb will be more sufficient, and the microstructure is more homogeneous. Nb element diffuses completely at 1400℃. Meanwhile, compression deformation and agglomeration phenomena of pores are observed in some pore nests. hot isostatic pressing （HIP） treatment can only efficiently decrease but not eliminate porosity completely.

关键词： powder metallurgy TiAl-based alloy hot pressing diffusion hot isostatic pressing

Effects of hot pressing on electric performances of Bi_(0.5)Sb_(1.5)Te_(3)

在线全文

学校读者我要写书评

暂无评论

Rare Metals 2006年第Z1期25卷 320-323页

作者： XIAO Bo CHEN Hui WU Borong ZHU Lei LIU Mingyi JIAN Xuyu LI Lin Institute for Energy Materials and Technology General Research Institute for Non-Ferrous MetalsBeijing 100088China Tianjin Institute of Power Sources Tianjin 300381China

The effects of hot pressing on electric performance and mechanical strength of Bi_(0.5)Sb_(1.5)Te_(3) thermoelectric material prepared through vacuum melting and milling were *** phase constituent and microstructure were analyzed by X-ray Diffraction and cold field emission Scanning Electric *** of the material on microstructure and electric performances are *** the rise of hot pressing temperature(from 300-500℃)and pressure(30-70 MPa),electric conductivity and power factor are ***,Bi_(0.5)Sb_(1.5)Te_(3) material can gain ideal thermoelectric performances and increased mechanical strength by hot pressing.

关键词： thermoelectric material hot pressing power factor electric conductivity

Densification behavior of high Nb containing TiAl alloys through reactive hot pressing

在线全文

学校读者我要写书评

暂无评论

Journal of University of Science and Technology Beijing 2007年第3期14卷 251-255页

作者： Yanhang Wang Junpin Lin Yuehui He Yanli Wang Guoliang Chen State Key Laboratory for Advanced Metals and Materials University of Science and Technology Beijing Beijing 100083 China State Key Laboratory for Powder Metallurgy Central South University Changsha 410083 China

Densification behavior of high Nb containing TiAl alloys through reactive hot pressing was investigated. The results showed that the density of the sample hot pressed at 1400°C could reach a near full density of 98.37%. However, the densification abnormality was observed at 1500°C. The diffusion of elemental Nb during microstructural evolution is an important aspect affecting densification, which will form pore nests. With the increase of hot pressing temperature, the diffusion of Nb becomes more adequate. HIP （hot isostatic pressing） treatment can only decrease porosity to some extent, but cannot eliminate it completely.

关键词： TiAl based alloy powder metallurgy densification hot pressing

Microstructure and thermoelectric properties of Bi_(0.5)Na_(0.02)Sb_(1.48-x)In_xTe_3 alloys fabricated by vacuum melting and hot pressing

在线全文

学校读者我要写书评

暂无评论

Rare Metals 2015年第11期34卷 770-775页

作者： Xing-Kai Duan Kong-Gang Hu Da-Hu Ma Wang-Nian Zhang Yue-Zhen Jiang Shu-Chao Guo Center for New Energy Materials Research School of Mechanical and Materials Engineering Jiujiang University

The Bi0.5Na0.02Sb1.48-xInxTe3alloys（x =0.02-0.20） were synthesized by vacuum melting and hot pressing methods at 753 K,60 MPa for 30 *** of Na and In dual partial substitutions for Sb on the thermoelectric properties were investigated from 300 to 500 *** Sb with Na and In can enhance the Seebeck coefficient effectively near room *** electrical resistivity of the Na and In dual-doping samples is higher within the whole test temperature *** Bi0.5Na0.02Sb1.48-xInxTe3samples（x = 0.02,0.06） play a great role in optimizing the thermal *** for the Bi0.5Na0.02Sb1.46In0.02Te3alloy,the minimum value of thermal conductivity reaches 0.53 W·m-1·K-1at 320 *** thermoelectric performance of the Na and In dualdoped samples is greatly improved,and a figure of merit ZT of 1.26 is achieved at 300 K for the Bi0.5Na0.02Sb1.42In0.06Te3,representing 26%enhancement with respect to ZT = 1.0 of the undoped sample.

关键词： Microstructure Dual doping hot pressing Thermal co

Microstructure and mechanical properties of Cu-B4C and CuAl-B4C composites produced by hot pressing

在线全文

学校读者我要写书评

暂无评论

Rare Metals 2019年第12期38卷 1169-1177页

作者： Zulkuf Balalan Furkan Gulan Mechanical Engineering Department Faculty of Engineering and ArchitectureUniversity of Bingol

Cu matrix composite materials reinforced with B4C particle at four different contents(1.5 wt%,3.0 wt%,4.5 wt% and 6.0 wt%) and also CuAl matrix composites with 13 wt% Al reinforced with B4C particle at four different contents(1.5 wt%,3.0 wt%,4.5 wt% and 6.0 wt%)were fabricated by hot pressing(HP) and a powder metallurgy(PM) *** samples were produced by keeping them at 880℃ at the constant pressure of 2.3×10~8 Pa for 6 *** density,microstructure and mechanical properties of the produced samples were *** microstructure and phase examinations were carried out by scanning electron microscope(SEM)and optical microscope(OM),energy-dispersive spectrometer(EDS) and X-ray diffractometer(XRD) *** hardness measurements,three-point bending test and impact test were conducted to determine the mechanical *** a result of the examinations,it was observed that the relative density values decreased with the increasing content of B4C and provided a relatively effective ***,it was homogeneously distributed in the produced ***,there was a considerable increase in the hardness and the bending strength of CuAl matrix specimens with Al addition.

关键词： Boron carbide hot pressing Mechanical properties Aluminum

Preparation of in situ and ex situ reinforced Fe–10Cr–1Cu–1Ni–1Mo–2C containing NbC particles by milling and hot pressing

在线全文

学校读者我要写书评

暂无评论

International Journal of Minerals,Metallurgy and Materials 2015年第2期22卷 157-166页

作者： Xiao-qiang Li Zi-yang Li Yong-quan Ye Ke Hu School of Mechanical and Automotive Engineering South China University of Technology

An in situ and ex situ reinforced powder metallurgy （PM） steel was prepared by the combination of high-energy ball milling and subsequent hot pressing of elemental mixed powders of Fe-10Cr-1Cu-1Ni-1Mo-2C by mass with the addition of NbC particles. A 40-h milling pretreatment makes the powder particles nearly equiaxed with an average diameter of-8 μm, and the ferrite grain size is refined to -6 nm. The sintered density reaches 99.0%-99.7% of the theoretical value when the sintering is conducted at temperatures greater than 1000℃ for 30 min. In the sintered bulk specimens, the formation of an in situ M7C3 （M = Cr, Fe, Mo） phase is confirmed. MTC3 carbides with several hundred nanometers in size are uniformly distributed in the matrix. Some ultra-fine second phases of 50-200 nm form around the ex situ NbC and in situ M7C3 particles. The sintered steel exhibits an excellent combination of hardness （〉 Hv 500） and compressive strength （2100-2420 MPa）.

关键词： steel powder metallurgy reinforcement ball milling hot pressing

Structure and magnetic properties of bulk nanocrystalline Nd-Fe-B permanent magnets prepared by hot pressing and hot deformation

在线全文

学校读者我要写书评

暂无评论

Journal of Rare Earths 2013年第7期31卷 674-678页

作者：宋杰岳明左建华张子瑞刘卫强张东涛张久兴郭朝晖李卫 College of Materials Science and Engineering Beijing University of Technology Division of Functional Materials Central Iron and Steel Research Institute

Structure and magnetic properties were studied for bulk nanocrystalline Nd-Fe-B permanent magnets that were prepared at 650 ℃ for 3 min under 300 MPa using the SPS-3.20-MK-V sintering machine and the hot pressed magnets were then submitted to hot deformation with height reduction of 50%, 60%, 70%, 80%, and 85%. Effects of height reduction （HR） and deformation temperature on the structure and magnetic properties of the magnets were investigated. The crystal structure was evaluated by means of X-ray diffraction （XRD） and the microstructure was observed by transmission electron microscopy （TEM）. The magnetic properties of the magnets were investigated by vibrating sample magnetometer （VSM）. As the height reduction increased, the remanence （Br） of the magnets increased first, peaks at 1.3 T with HR=60%, then decreased again, and the coercivity （Hci） of the magnets decreased monotonically. On the other hand, as the deformation temperature increased, the Br of the magnets increased first, peaks at 1.36 T with HR=60%, then decreased again, and the H^i of the magnets decreased monotonically. Under optimal conditions, the hot deformed magnet possessed excellent magnetic properties as Brl.36 T, Hci=1143 kA/m, and （BH）max=370 kJ/m3, suggesting the good potential of the magnets in practical applications.

关键词： nanocrystalline Nd-Fe-B magnets hot pressing hot deformation microstructure magnetic properties rare earths

Effect of hot pressing on Microstructure and Mechanical Properties of Bulk Nanocrystalline Fe_3Al Materials Containing Manganese Element

在线全文

学校读者我要写书评

暂无评论

Journal of Iron and Steel Research International 2011年第3期18卷 65-71页

作者： LI Yu-feng LA Pei-qing WEI Yu-peng LU Yang YANG Yang State Key Laboratory of Gansu Advanced Nonferrous Materials Lanzhou University of TechnologyLanzhou 730050GansuChina

Bulk nanocrystalline Fe3Al materials containing manganese of 10% were prepared by aluminothermic *** pressing of those materials was performed at different temperatures and *** microstructures of the alloy were investigated by optical microscope（OM） and electron probe microanalyzer（EPMA）.The grain sizes of the materials were analyzed by X-ray diffraction（XRD） and transmission electron microscope（TEM）.The results showed that the grain sizes of the materials increase after hot *** grain sizes of the materials decrease with increasing the hot pressing times at the same temperature and the grain sizes of the materials increase with increasing hot pressing temperatures at identical *** hardness and compressibility of the materials were also *** results showed that the hardness decreases with increasing hot pressing times at 800 ℃ and hardness increases with increasing the hot pressing *** variation of hardness with grain size of the nanocrystalline Fe3Al materials after hot pressing is contrary to the Hall-Petch *** materials are not broken during hot pressing and exhibit good plasticity and compressibility.

关键词： hot pressing Fe3Al nanostructure material microstructure mechanical property