High temperature induced“glaze”layer formed in HVOF-sprayed NiCrWMoCuCBFe coating and its wear reduction mechanism

Friction 2022年第9期10卷 1424-1438页

作者： Yijing WANG Xiaoqin ZHAO Enkang HAO Zhenyu BU Yulong AN Huidi ZHOU Jianmin CHEN State Key Laboratory of Solid Lubrication Lanzhou Institute of Chemical PhysicsChinese Academy of SciencesLanzhou 730000China Center of Materials Science and Optoelectronics Engineering University of Chinese Academy of SciencesBeijing 100049China

The in-situ formation of oxides on alloy surface induced by high temperature can effectively reduce wear and resist oxidation.In consideration of the solid solution strengthening effect and great oxidation resistance of additional elements at elevated temperature,the NiCrWMoCuCBFe coating was prepared by high velocity oxygen flame(HVOF)spraying technology,and its tribological behavior was scrutinized from 25 to 800°C.By means of high temperature Vickers hardness tester and high temperature X-ray diffractometer,the mechanical properties and microstructures of NiCrWMoCuCBFe coating were measured.And the effect of the mechanical properties and microstructures of the coating on tribological performance was discussed in detail.The results showed both its friction coefficient(0.37)and wear rate(5.067×10^(−6)mm^(3)·N^(−1)·m^(−1))at 800℃ were the lowest,which was mainly related to the formation of“glaze”layer on the coating surface at high temperature.The glaze layer consisted of two parts,which were NiCr_(2)O_(4)oxide film with the ability of interlaminar slip formed in the outer layer and nano-grains existed in the inner layer.Worth mentioning,these nano-grains provided bearing capability while the oxide film was vital to reduce wear rate and friction coefficient.As the ambient temperature increased,many hard oxides were produced on the wear scars,including NiO,Cr_(2)O_(3),MoO_(3),and Mo_(2)C.They can improve tribological and mechanical properties of NiCrWMoCuCBFe coating at a wide temperature range.

关键词： high temperature wear and friction NiCrWMoCuCBFe coating in-situ oxidation glaze layer mechanical properties

来源：

维普期刊数据库评论

在线全文

维普期刊数据库

学校读者我要写书评

暂无评论

Effect of heat treatment temperature of the glaze lager on the structure and the formaldehyde removal performance of an interior wall tile

引用

International Journal of Minerals,Metallurgy and Materials 2022年第11期29卷 2079-2085页

作者： Ruqin Gao Yingrui Huang Enhui Wang Xinmei Hou Lu Pan Guoting Li Bingtao Liu School of Environmental Science and Engineering North China University of Water Resources and Electric PowerZhengzhou 450046China Collaborative Innovation Center of Steel Technology University of Science and Technology BeijingBeijing 100083China

With the improvement of people’s living standards,a large number of petroleum products,daily necessities and decorations that can produce volatile organic compounds are used in decoration,which seriously affects the indoor air quality.Interior decoration materials have become a research hotspot in recent years.The purpose of this paper is to develop a kind of interior wall material with good indoor formaldehyde removal effect,easily using,and low cost.In this paper,combining different heat treatment temperatures of the glaze layer,tourmaline/diatomite-based interior wall tiles were prepared by ultrafine grinding,solid sintering,and low temperature calcination.The glaze layer under different heat treatment temperatures was characterized by thermogravimetric-differential thermal analysis,X-ray diffraction,and scanning electron microscope.The influences of heat treatment temperature on the microscopic morphology and structure of the glaze layer were analyzed.Taking formaldehyde as the target degradation product,the effects of tourmaline/diatomite-based interior wall tiles on the removal of formaldehyde under different heat treatment temperatures of the glaze layer were investigated.The results showed that with the increase in heat treatment temperature,the original pores of diatomite decreased,the specific surface area decreased,and the structure of tourmaline changed.At 850℃,the surface structure of the material was slightly damaged,the strength was increased,and the removal effect of formaldehyde was better.In a 1 m^(3) environmental chamber,the formaldehyde removal rate reached 73.6%in 300 min.When the temperature was increased to 950℃ and above,diatomite and the structure of tourmaline were destroyed,and the ability of the material to adsorb and degrade formaldehyde decreased.

关键词： diatomite tourmaline/diatomite-based interior wall tiles glaze layer heat treatment temperature formaldehyde adsorption and degradation

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

Improving high-temperature wear resistance of NiCr matrix self-lubricating composites by controlling oxidation and surface texturing

引用

Journal of Materials Science & Technology 2022年第36期131卷 253-263页

作者： Xuan Kong Wenyao Sun Qunchang Wang Minghui Chen Tao Zhang Fuhui Wang Shenyang National Laboratory for Materials Science Northeastern UniversityShenyang 110819China

Self-lubricating composites(SLCs)are widely used in the fields of aerospace and marine,but the conventional NiCr matrix SLCs with sulfide as solid lubricant often suffer from low wear resistance at high temperatures.In view of its high affinity with oxygen and also the high oxidation rate,appropriate amount of nano Ti was added to NiCr-WS_(2)composites prepared by spark plasma sintering(SPS)to adjust the oxidation behavior and surface texture.When exposed to high temperature,Ti was preferentially oxidized in comparison to Ni and Cr,resulting in abundant TiO_(2)protrusions and microdimples on the surface,i.***.in situ surface texturing.Besides,TiO_(2)was of high chemical activity and readily to react with other oxide debris during high temperature sliding process to form compounds of NiTiO_(3)and CrTi_(2)O_(5).The high chemical activity of oxide debris that was conducive to sintering,combining with the special surface texture that stores as many wear debris as possible,promoted the rapid formation of a protective glaze layer on the sliding surface.The NiCr-WS_(2)-Ti composite exhibited low friction coefficient but high wear resistance at elevated temperatures.Especially at 800℃,it presented a wear rate of as low as(2.1±0.3)×10^(-5)mm^3N-1m^(-1),accounting for only 2.7%of that of NiCr-WS_(2)composite.

关键词： Self-lubricating composites High temperature oxidation glaze layer Surface texturing

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

在线全文

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

在线全文

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：