Deuterium retention and Physical Sputtering of Low Activation Ferritic Steel

Plasma Science and Technology 2005年第2期7卷 2737-2740页

作者： T.Hino K.Yamaguchi Y.Yamauchi Y.Hirohata K.Tsuzuki Y.Kusama Department of Nuclear Engineering Hokkaido University Sapporo060-8628 JapanDepartment of Nuclear Engineering Hokkaido UniversitySapporo060-8628 JapanDepartment of Nuclear Engineering Hokkaido UniversitySapporo060-8628 JapanDepartment of Nuclear Engineering Hokkaido UniversitySapporo060-8628 JapanJapan Atomic Energy Research Institute NakaIbaraki-ken311-0193 JapanJapan Atomic Energy Research Institute NakaIbaraki-ken311-0193 Japan

Low activation materials have to be developed toward fusion demonstrationreactors. Ferritic steel, vanadium alloy and SiC/SiC composite are candidate materials of the firstwall, vacuum vessel and blanket components, respectively. Although changes of mechanical-thermalproperties owing to neutron irradiation have been investigated so far, there is little data for theplasma material interactions, such as fuel hydrogen retention and erosion. In the present study,deuterium retention and physical sputtering of low activation ferritic steel, F82H, wereinvestigated by using deuterium ion irradiation apparatus. After a ferritic steel sample wasirradiated by 1.7 keV D^+ ions, the weight loss was measured to obtain the physical sputteringyield. The sputtering yield was 0.04, comparable to that of stainless steel. In order to obtain theretained amount of deuterium, technique of thermal desorption spectroscopy (TDS) was employed to theirradiated sample. The retained deuterium desorbed at temperature ranging from 450 K to 700 K, inthe forms of DHO, D_2, D_2O and hydrocarbons. Hence, the deuterium retained can be reduced by bakingwith a relatively low temperature. The fluence dependence of retained amount of deuterium wasmeasured by changing the ion fluence. In the ferritic steel without mechanical polish, the retainedamount was large even when the fluence was low. In such a case, a large amount of deuterium wastrapped in the surface oxide layer containing O and C. When the fluence was large, the thickness ofsurface oxide layer was reduced by the ion sputtering, and then the retained amount in the oxidelayer decreased. In the case of a high fluence, the retained amount of deuterium became comparableto that of ferritic steel with mechanical polish or SS 316 L, and one order of magnitude smallerthan that of graphite. When the ferritic steel is used, it is required to remove the surface oxidelayer for reduction of fuel hydrogen retention. Ferritic steel sample was exposed to the envi

关键词： ferritic steel fuel hydrogen retention sputtering yield first wall fusionreactor

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：