The Effective Surface Metallization of Hollow Glass Microspheres for Flexible electromagnetic shielding film

Journal of Wuhan University of Technology(Materials Science) 2022年第5期37卷 779-786页

作者： BU Fan SONG Pengcheng LIU Yahui WANG Jun WU Xiyuan LIU Lei XU Chuanhua ZHAGN Jianfeng College of Mechanics and Materials Hohai UniversityNanjing 21l100China Sinosteel Maanshan New Material Technology Co. LtdMaanshan 243000China

The surface of hollow glass microspheres (HGMs) was roughened by a HCl+NH_(4)F strategy,which achieved a broken ratio as 16.10%,and then metallized by electroless plating by Co nanoparticles up to 90 wt% (abbreviated as Co-HGMs).The average grain size of Co was measured to range from 0.4 to 0.5 μ*** Co-HGMs were mixed with liquid silicone rubber and xylene,and cured on a perspex plate applicable for flexible electromagnetic *** attentive parameter optimization,a film about 0.836 mm in thickness was obtained with a density of 0.729 g/cm^(3),showing a shielding effectiveness of 15.2 dB in the X-band (8.2-12.4 GHz) at room temperature,which was ascribed to the formation of a conductive network of Co-HGMs inside the ***,the tensile strength of 0.89 MPa at an elongation ratio of 194.5% was also obtained,showing good mechanical properties and tensile strength.

关键词： hollow glass microspheres(HGMs) electroless plating electromagnetic shielding film flexible film lightweight materials

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：