Preparation and Characterization of Nano-Particles PZT Ferroelectric Thin Films by RF-Magnetron Sputtering

Transactions of Tianjin University 2006年第2期12卷 96-99页

作者：樊攀峰张之圣胡明刘志刚 School of Electronic Information Engineering Tianjin University Tianjin 300072China

Pt/Ti bottom electrodes were fabricated on SiO2/Si substrates by magnetron dual-facingtarget sputtering system. Lead zirconate titanate（PZT） thin films were deposited on Pt/Ti/SiO2/Si substrates by radio frequency （RF） magnetron sputtering system. The thickness of PZT thin films which were deposited for 5 h was about 800 nm. XRD spectra show that PZT thin films deposited in Ar ambience and rapid-thermal-annealed for 20 min at 700 ℃ have good crystallization behavior and perovskite structure. AFM micrographs show that mean diameter of crystallites is 70 nm and surface structures of PZT thin films are uniform and dense. Raw mean, root mean square roughness and mean roughness of PZT thin films are 34..357 rim, 2. 479 nm and 1. 954 nm respectively. As test frequency is 1 kHz, dielectric constant of PZT thin films is 327.5. electric hysteresis loop shows that coercive field strength, residual polarization strength and spontaneous polarization strength of PZT thin films are 50 kV/cm, 10μC/cm^2 and 13μC/cm^2 respectively.

关键词： PZT thin films radio frequency magnetron sputtering perovskite structure electric hysteresis loop

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：