Effects of direct ultrasonic treatment on microstructure and elongation of semi-solid Sn-62Bi alloy

China Foundry 2015年第3期12卷 163-168页

作者： Hui-ting Zheng Yong-jun Hu Ren-jie Li Hong-huan Yang Xiao-yan Sun Zhi-hao Li School of Materials and Energy Guangdong University of Technology

A new direct ultrasonic treatment(DUT) setup with the ultrasonic horn placed in the horizontal direction was developed and used in the preparation of semi-solid Sn-62 Bi slurry. The influence of DUT temperature on microstructure and properties of Sn-62 Bi alloy were studied. The test results of XRD showed that the semi-solid Sn-62 Bi alloy obtained by the DUT process exhibits pronounced preferential orientation of Bi(2 0 2), Bi(-1 1 1), Bi(-2 0 1), Sn(1 1 0) and Sn(2 2 0) planes. Compared to the conventional liquid casting Sn-62 Bi alloy without DUT, it was discovered that the primary Bi blocks of semi-solid Sn-62 Bi alloy prepared with the DUT process distribute more homogeneously and are smaller. With the treatment by ultrasonic vibration in the semi-solid state for 120 s, the higher the primary Bi phase fraction in the slurry, the smaller the size of primary semi-solid Bi blocks formed after solidification. The average side length of the primary Bi blocks was from 30 μm to 80 μm. The elongation of Sn-62 Bi alloy treated by DUT for 120 s at 145 °C is 43.21%, reflecting a distinctly improvement by 129.10%, as compared to the conventional liquid casting Sn-62 Bi alloy without DUT. This indicates that DUT process could improve dramatically the ductility of Sn-62 Bi alloys content. The microstructure evolution mechanism of semi-solid Sn-62 Bi alloy slurry was also analyzed.

关键词： direct ultrasonic treatment semi-solid Sn-Bi microstructure elongation

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：