Preparation and Properties of foam glass-ceramic from diatomite

Journal of Wuhan University of Technology(Materials Science) 2018年第2期33卷 273-277页

作者： Ivanov KS Institute of the Earth Cryosphere Siberian Branch of Russian Academy of Sciences Tyumen 625026 Russia Tyumen Industrial University Tyumen 625000 Russia

The results of the study of raw mix preparation and foam glass-ceramics production using diatomite as a raw material were presented in the following article. A mixture of diatomite and 40% NaOH solution was subjected to heating at a constant temperature of 775 ℃. Samples of foam glass-ceramic from diatomite with an average density of 290-580 kg/m^3, compressive strength of 1.7-7.8 MPa and thermal conductivity of 0.08-0.14 W/（m·K） were obtained. The investigations have shown that the hydrothermal pretreatment of mixture at the temperature of 90 ℃ may lead to the acceleration of the leaching of amorphous SiO_2 from diatomite. It was discovered that the resulting soluble alkali silicates promote the process of foaming during heating and reduce the average density of the obtained samples. The optimal duration of the leaching process was estimated to be 30 minutes, which corresponds to the yield of SiO_2 equal to 42.5% by the weight of dry diatomite.

关键词： diatomite liquid glass foam glass-ceramics

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：