Investigation on the Structure and curing Performances of Secondary Amine Terminated Hyperbranched Poly(ester-amine)s

引用

Chinese Journal of Structural Chemistry 2010年第7期29卷 1115-1121页

作者： JIN Xin TANG Li-Ming YOU Hu Laboratory of Advanced Materials Department of Chemical Engineering Tsinghua University Beijing 100084 China

Three secondary amine terminated hyperbranched poly（ester-amine）s （defined as HPEA1, HPEA2 and HPEA3） were synthesized from piperazine （A2） and trimethylolpropane triacrylate （TMPTA, B3） at their molar ratios of 2.5：1, 2.25：1 and 2.0：1, respectively. The polymers were analyzed by 1H NMR, GPC, DSC and TGA. The results indicated that the ratio of secondary amine to tertiary amine and the content of secondary amine decreased, while the molecular weight, molecular weight distribution and glass transition temperature （Tg） increased from HPEA1 to HPEA3. Due to their reactive terminal groups and flexible chains, these polymers further reacted with an epoxy resin （E51） to form cured films under ambient conditions. With increasing the ratio between secondary amine groups and epoxy groups from 1：2 to 2：1, the gel content, film hardness and onset decomposing temperature of the cured samples increased. The good film performances should make the polymers as the components of non-solvent coating materials.

关键词： hyperbranched poly(ester-amine) structure epoxy resin curing film

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：