Effect of chromium on hot corrosion behavior of arc-sprayed NiCr coatings

China Welding 2024年第1期33卷 1-6页

作者：王旭张海燕魏炜高站起尼军杰黄智泉 Zhengzhou Research Institute of Mechanical Engineering Co. Ltd.Zhengzhou450001China

In this article,NiCr coatings with chromium content of 13%,27%and 41%were prepared by arc *** were exposed in molten salts(NaCl-Na_(2)SO_(4))at 800℃for 200 *** effect of chromium content on the hot corrosion behavior of the coatings was in-vestigated.X-ray diffraction(XRD)and scanning electron microscope with energy dispersion spectrum(SEM-EDS)were used to analyze the phase compositions,morphologies and chemical compositions of the *** results show that NiCr13 coating exhibited the worst hot corrosion resistance due to the low chromium content,which resulted in NiO being the major reaction *** should be noted that the hot corrosion resistance of NiCr27 coating was better than that of NiCr41 *** basic fluxing of Cr_(2)O_(3) lowered its protection during the hot corrosion process and led to the formation of porous Cr_(2)O_(3) on the NiCr41 *** molten salts accelerated the oxidation reac-tion resulting in thicker and porous oxide scales formed on the surfaces of coatings.

关键词： NiCr coatings arc spraying hot corrosion Na_(2)SO_(4)-NaCl basic fluxing

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：