Tribological properties of TiAlN-coated cermets

Rare Metals 2009年第1期28卷 57-62页

作者： ZHENG Liyun ZHAO Lixin XIONG Weihao Key Laboratory of Resource Explore Research of Hebei Province Hebei University of Engineering Handan 056038 China College of Materials Science and Engineering Huazhong University of Science and Technology Wuhan 430074 China

Ti（C,N）-based cermets were coated with TiAlN using multi-arc ion plating technology. Sliding wear tests were performed on the coated cermets. The microstructure and morphologies of the coated cermets before and after friction and wear tests were characterized. The results show that the TiAlN coating surface was smooth and its root mean square roughness was 16.6 nm. The hardness （HK） of TiAlN coating layers reached approximately 3200 and the critical load （Lc） under which the coating failure occurred was 59 N. The sliding wear test results show that the friction coefficients of the TiAlN-coated cermets were lower than that of the cermets without any coating. Under the same load, the adhesion phenomenon of the counterpart materials on the specimens was improved and the mean friction coefficient increased with increasing sliding velocity. When the sliding velocity was 0.26 m·s^-1, the mass of the coated cermets reduced. At the same sliding velocity, the average friction coefficient of the TiAlN-coated cerrnets was lower under a higher load. The wear mechanisms of the TiAlN-coated cermets were mainly adhesive and abrasive wear.

关键词： cermets tribological properties wear tiain coating

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：