Unveiling the Residual Stresses,Local Micromechanical Properties and Crystallographic Texture in a ti-6al-4v Weld Joint

引用

Acta Metallurgica Sinica(English Letters) 2021年第7期34卷 997-1006页

作者： B.Mehdi R.Badji v.Ji B.alili D.Bradai W.Bedjaoui F.Deschaux-Beaume F.Brisset Laboratoire de Physique Des Matériaux Facul téde PhysiqueUniversitéDes Sciences Et de La Technologie Houari Boumediene16111 AlgerAlgérie Research Center in Industrial Technologies CRti P.O.Box64CheragaAlgeria ICMMO/SP2M UniversitéParis-Saclay LMGC University of MontpellierCNRSMontpellierFrance

In this work,the micromechanical properties,crystallographic texture,welding residual stresses and their evolution after plastic strain were investigated in a ti-6al-4v alloy tungsten inert gas weld *** was found that the welding process affected the Young modulus and microhardness values in bothαandβphases in the different regions of the weld *** highest microhardness and Young modulus values of a phase were recorded in the heat-affected zone,whereas the highest values of these characteristics for theβphase were found in the fusion zone(FZ).The change in the micro mechanical properties was accompanied by a change in the crystallographic texture components of the dominant a phase from(0001)and(11-20)components in the base material to(10-10)and(11-20)components in the *** introduction of tensile testing resulted in a continuous stress relaxation and improved the weld joint performances.

关键词： ti-6al-4 v Tungsten inert gas(tiG)weld Residual stress Local mechanical properties Crystallographic texture

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

Study of diffusion bonding of ti-6al-4v and ZQSn10-10 with metal interlayer

引用

China Welding 2008年第1期17卷 36-39页

作者：赵涣凌赵贺冯吉才宋敏霞赵熹华 School of Materials Science and Engineering Jilin University State Key Laboratory of Advanced Welding Production Technology Harbin Institute of Technology

The diffusion bonding was carried out to join ti alloy （ti-6al-4v） and tin-bronze （ ZQSn10-10 ） with Ni and Ni ＋ Cu interlayer. The microstructures of the diffusion bonded joints were analyzed by scanning electron microscope （SEM）, energy dispersive spectroscopy （ EDS ） and X-ray diffraction （ XRD ）. The results show that when the interlayer is Ni or Ni ＋ Cu transition metals both could effectively prevent the diffusion between ti and Cu and avoid the formation of the Cu-ti intermetallic compounds （Cu3ti, Cuti etc. ）. But the Ni-ti intermetallic compounds （Niti, Ni3ti） are formed on the ti-6al-4v/Ni interface. When the interlayer is Ni, the optimum bonding parameters are 830 ℃/10 MPa/30 min. And when the interlayer is Ni ＋ Cu, the optimum bonding parameters are 850 ℃/10 MPa/20 min. With the optimum bonding parameters, the tensile strength of the joints with Ni and Ni ＋ Cu interlayer both are 155.8 MPa, which is 65 percent of the strength of ZQSn10-10 base metal.

关键词： diffusion bonding ti-6al-4 v tin-bronze metal interlayer intermetallic compound

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：