Advanced Powder Materials 2023年第1期2卷 35-42页

作者： Aidong Xia Buhao Zhang Jie Yin Xiao Chen Sea-Hoon Lee Xuejian Liu Zhengren Huang State Key Laboratory of High Performance Ceramics and Superfine Microstructures Shanghai Institute of CeramicsChinese Academy of SciencesShanghai 200050China Ningbo Institute of Materials Technology and Engineering Chinese Academy of SciencesNingbo 315201China College of Materials Science and Opto-Electronic Technology University of Chinese Academy of SciencesBeijing 100049China Ceramic Materials Division Korea Institute of Materials ScienceChangwon 51508Republic of Korea

ZrB_(2)/SiC–AlN nanoceramic composites were densified at 1950℃ by hot pressing using an organic-precursorderived SiC and commercially available AlN and ZrB_(2).A cross-scale microstructure was constructed by distributing the ZrB_(2) secondary phase(~421 nm)within the SiC–AlN solid solution *** substructure of the SiC–AlN matrix was agglomerated by nanograins with an average size of only 62 ***_(2) connected around the majority of pores within the SiC–AlN matrix and contributed to the formation of numerous weak interfacial bonding,resulting in improved strength and *** highest flexural strength and fracture toughness of 579±52 MPa and 6.7±0.1 MPa m^(1/2) were obtained from a 10 wt%-ZrB2/SiC–AlN sample,*** high concentration of grain boundaries of the ZrB2/SiC–AlN nanoceramic composites resulted in heat insulation *** thermal diffusivity and conductivity were 3.6 mm^(2)·s^(-1) and 14.3 W⋅(m·K)^(-1) at 1400℃,respectively,while the electrical resistivity was 3.9×10^(3)Ω·cm for the 10 wt%-ZrB_(2)/SiC–AlN sample.

关键词： Nanoceramic composites Precursor-derived ceramics SiC-AlN solid Solution Mechanical properties thermal and electrical properties

来源：

维普期刊数据库评论

在线全文

维普期刊数据库

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：