tape casting of al_2o_3-tib_2/al_2o_3-nano-tic multilayer composites

Journal of Materials Science & Technology 1997年第4期13卷 324-326页

作者： Yuping ZENG Dongliang JIANG Shouhong TAN and Jingkun GUo(Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 200050, China) Shanghai Institute of Ceramics Chinese Academy of Sciences Shanghai 200050 China

Ceramic tapes, containing al2o3-25 wt pct tib2(B) and al2o3-25 wt pct nano-tic (c), have been obtained by tape casting process. Numerous tapes (about 60～80 tapes) were prepared by stacking in turn the composition (B) and (C), laminating under 10 MPa pressure, eliminating the solvent and burning out the polymer additives. The final green bodies were hot pressed at 1750℃ and 30 MPa. The composite has a bending strength of 568 MPa and a fracture toughness of 5.8 M Pa·m1/2. SEM analysis exhibits that al2o3 particle growth was inhibited by tic particles in C. but tib2 particles could not hinder al2o3 growth in B. The curves of GTA indicates that all organic additives could be removed completely above 600℃

关键词： nano tib al tape casting of al2o3-tib2/al2o3-nano-tic multilayer composites tic

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：