Optimization of sintering parameters for fabrication of Ag-sheathed FeSe superconducting wires

Rare Metals 2018年第5期37卷 433-438页

作者： Jian-Qing Feng Sheng-Nan Zhang Ji-Xing Liu Bo-Tao Shao Cheng-Shan Li Ming Liang Ping-Xiang Zhang superconducting Materials Research Center Northwest Institute for Non-Ferrous Metal Research School of Materials Science and Engineering Northeastern University School of Materials Science and Engineering Xi'an University of Technology

Ag-sheathed Fe1.05Se superconducting wires were fabricated with ex-situ powder in tube （PIT） process. Fe and Se powders with molar ratio of 1.05 were firstly mixed and sintered under 600 ℃ for 12 h to form precursor powders. Owing to the complex Fe-Se binary phase diagram, both superconducting tetragonal FeSe and nonsuperconducting hexagonal FeSe could be formed simultaneously during sintering. Aiming at the reduction of hexagonal FeSe phase content and higher superconducting phase volume, the influences of key parameters, including sintering time, cooling rate and heating rate, on the phase composition of sintered wires were systematically studied. Optimal sintering parameters are obtained, and the maximum tetragonal FeSe phase content of ~ 97% is achieved. Meanwhile, the effects of packing density of precursor powders on the phase composition of final wires were also discussed. Owing to the shorter length of diffusion path, more tetragonal FeSe was formed with higher packing density. The superconducting transition signal with critical temperature of ~ 7.5 K was obtained, which proved the effectiveness of our optimal sintering process.

关键词： Superconductors FeSe Powder in tube Phase composition superconducting transition

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

Extraordinary terahertz transmission through subwavelength spindle-like apertures in NbN film

引用

Chinese Physics B 2014年第1期23卷 230-233页

作者：郑小睿程飞吴敬波金飚兵朱北沂 National Laboratory for Superconductivity Institute of Physics and Beijing National Laboratory tbr Condensed Matter Physics Chinese Academy of Sciences Beijing 100190 China Research Institute of Superconductor Electronics (RISE) School of Electronic Science and Engineering Nanjing University Nanfing 210093 China

We studied numerically the temperature dependent extraordinary terahertz transmission through niobium nitride(NbN) film perforated with subwavelength spindle-like apertures. Both the resonant frequency and intensity of extraordinary terahertz transmission peaks can be greatly modified by the transition of NbN film from the normal state to the superconducting state. An enhancement of the(±1, 0) NbN/magnesium oxide(MgO) peak intensity as high as 200% is demonstrated due to the combined contribution of both the superconducting transition and the excitation of localized surface plasmons(LSPs) around the apertures. The extraordinary terahertz transmission through spindle-like hole arrays patterned on the NbN film can pave the way for us to explore novel active tuning devices.

关键词： extraordinary terahertz transmission superconducting transition spindle-like apertures localized surface plasmon mode

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

室温下过搀杂Bi2212高温超导单晶的化学相分离

引用

低温物理学报 2003年第S1期25卷 486-490页

作者：吴孝松吕力张殿林宣毅陶宏杰中国科学院物理研究所极端条件实验室中国科学院物理研究所超导国家重点实验室中国科学院物理研究所超导国家重点实验室北京100080

我们用高灵敏度的交流磁强计研究了Bi2 2 1 2高温超导单晶的超导转变行为 ,发现对过搀杂的单晶样品 ,高温退火处理后立即测量 ,磁化表现为陡峭的超导转变 .但是放置一段时间 (数周)后 ,磁化曲线出现多个转变 ,并且再次高温退火能将其恢... 详细信息

我们用高灵敏度的交流磁强计研究了Bi2 2 1 2高温超导单晶的超导转变行为 ,发现对过搀杂的单晶样品 ,高温退火处理后立即测量 ,磁化表现为陡峭的超导转变 .但是放置一段时间 (数周)后 ,磁化曲线出现多个转变 ,并且再次高温退火能将其恢复为单一转变 .说明即使是很均匀的单相 ,随着时间的推移 ,也会出现相分离现象 .这一结果表明 ,在室温下 ,单晶中的氧原子仍然能够移动 ,而且倾向于重新排布形成不同的相 .新形成的相的的磁化曲线有约瑟夫森弱联的特征 ,暗示新相是以小的团簇形势存在 ,团簇之间以约瑟夫森弱联耦合起来 .另一方面 ,对最佳搀杂的单晶样品 ,没有观察到相分离现象 .

关键词： high temperature superconductor chemical phase separation Bi2212 superconducting transition

来源：

同方期刊数据库评论

在线全文

同方期刊数据库

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

在线全文

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

在线全文

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：