Force-sensitive properties of FeCuNbSiB powder/silicone rubber composite films

Rare Metals 2016年第10期35卷 784-789页

作者： Jia Zhou Zheng-Hou Zhu Xiao-Min Li Kang Du Bao-Ying Qiao Yuan Fu School of Materials and Engineering Nanchang University

Composite films of different contents were prepared by Fe73.5Cu1Nb3Si13.5B9 powder as compound phase and silicone rubber as matrix phase. The thickness of film is 200 μm. Values of impedance, Z, under pressure stress were measured by TH2816LCR digital bridge. LYYL-500N high-grade-type microcomputer control pressure testing machine was used to conduct program control loading with a speed of 0.1 mm·min^-1. The results show that composite films of different contents （25 vol%, 30 vol%, and 35 vol%） have excellent force-sensitive properties in both loading process and unloading process, especially when the stress is below 0.2 MPa, the stress- impedance （SI） and ＋｜k｜ values of composite films are much higher than that in the range of 0.2-1.0 MPa. The force- sensitive properties of loading process are superior to unloading process. While the frequency is 1 kHz, the force-sensitive properties of composite films are better than 50 kHz. The optimal temperature of powder heat treatment is 500 ℃. Composite film which was prepared by this kind of powder has a good force-sensitive property.

关键词： Composite films stress-impedance effect Force-sensitive properties

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：