microstructure and mechanical properties of a spray-formed superalloy

Acta Metallurgica Sinica(English Letters) 2014年第6期27卷 1063-1069页

作者： Fuwei Kang Fuyang Cao Xuemin Zhang Hongyan Yue Yicheng Feng School of Materials Science and Engineering Harbin University of Science and Technology School of Materials Science and Engineering Harbin Institute of Technology

The microstructural evolution and mechanical properties of a spray-formed superalloy were studied in this paper. Based on a better understanding of the microstructural evolution of the spray-formed superalloy during solution treatment, an optimum solution treatment process was obtained, namely, at 1,140 °C for 6 h, and air cooling（AC）. The effects of the ageing treatments on the mechanical properties of the post-solution-treated spray-formed superalloy were evaluated using ageing harden curves and tensile testing. The results indicated that the maximum hardness value was achieved at 850 °C for 8 h, AC. Due to co-precipitation of primary and secondary c0 precipitates during the heat treatment,the spray-formed superalloy obtained an excellent combination of yield strength（YS = 1,110 MPa）, ultimate tensile strength（UTS = 1,503 MPa）, ductility（elongation, EL = 21%） and excellent stress rupture properties at 650 °C（UTS = 1,209 MPa, EL = 15.8%）. The heat treatment also improved the rupture life at 650 °C/950 MPa and 750 °C/539 MPa up to 140 h without rupturing. The tensile-fractured surfaces exhibit ductile transgranular failure feature. The optimum heat treatment process was determined to be 1,140 °C/6 h＋850 °C/8 h＋AC.

关键词： spray-formed superalloy microstructure ageing harden mechanical properties

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：