Microstructure Characteristics of Inconel 625 Superalloy Manufactured by selective laser Melting

Journal of Materials Science & Technology 2015年第9期31卷 946-952页

作者： Shuai Li Qingsong Wei Yusheng Shi Zicheng Zhu Danqing Zhang State Key Laboratory of Die & Mould Technology Huazhong University of Science and Technology NTU Additive Manufacture Centre Nanyang Technological University

selective laser melting （SLM）, an additive manufacturing process, is capable of manufacturing metallic parts with complex shapes directly from computer-aided design （CAD） models. SLM parts are created on a layer-by-layer manner, making it more flexible than traditional material processing techniques, in this paper, Inconel 625 alloy, a widely used material in the aerospace industry, were chosen as the build material. Scanning electron microscopy （SEM）, electron back scattering diffraction （EBSD） and X-ray diffraction （XRD） analysis techniques were employed to analyze its microstructure. It was observed that the molten pool was composed of elongated columnar crystal, Due to the rapid cooling speed, the primary dendrite arm space was approximately 0.5 μm and the hardness of SLM state was very high （343 HV）. The inverse pole figure （IPF） indicated that the growing orientation of the most grains was 〈001〉 due to the epitaxial growth and heat conduction. The XRD results revealed that the austenite structure with large lattice distortion was fully formed. No carbides or precipitated phases were found. After heat treatment the grains grew into two microstructures with distinct morphological characters, namely, rectangular grains and limited in the molten pool, and equiaxed grains along the molten boundaries. Upon experiencing the heat treatment, MC carbides with triangular shapes gradually precipitated. The results also identified that a large number of zigzag grain boundaries were formed. In this study, the grain formation and microstructure, and the laws of the molten pool evolution were also analyzed and discussed,

关键词： selective laser meltingnickel based superalloytexturelattice constantzigzag grain boundary

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：