Influence of Surface Finishing on High-Temperature Oxidation of AISI Type 444 Ferritic Stainless Steel Used in sofc stacks

引用

Acta Metallurgica Sinica(English Letters) 2017年第8期30卷 697-711页

作者： Valeria Bongiorno Paolo Piccardo Simone Anelli Roberto Spotorno Laboratorio di Metallurgia e Materiali - Dipartimento di Chimica e Chimica Industriale (LMM-DCCI) Universita degli Studi di Genova Via Dodecaneso 31 16146 GenoaItaly

This research is focused on the study of the samples, approximatively 15 × 30 mm^2 sized, that were mechanically cut from two sheets （0.4 and 0.2 mm thick, respectively） of AIS1444 Type ferritic stainless steel （FSS）（DIN 1.4521, Eu designation X2CrMoTil8-2）; this material was in the ＇as-rolled＇ state. Part of these specimens were treated superficially on one side using abrasive SiC papers with different average grit sizes （i.e., 46.2, 30.2, 18.3 gm） and diamond suspension （up to 1 tim） in order to obtain various surface roughness. Both the ＇as-rolled＇ and superficially treated samples were then aged in a muffle fumace in static air according to a thermal cycle corresponding to the curing phase of an experimental glass used as sealing in the solid oxide fuel cell stacks. After aging, the chemical compositions and mor- phological peculiarities of the scale formed depending on the thickness of the samples and their surface state were studied by scanning electron microscopy, energy-dispersive spectroscopy, micro-Raman spectroscopy, bright field light optical microscopy. The obtained results show that all scales formed consist of an inner Cr2O3 subscale and an outer （Mn,Cr）3O4 spinel layer; the relationship between FSS grain size and scale microstructural features is consistent on the samples with mirror-like surface only; the scale thicknesses on SiC grinded samples are comparable; the scales covering the ＇as-rolled＇ surfaces are morphologically similar to those grown on the surfaces finished with the 30.2 and 18.3 μm SiC papers, and their thicknesses show an intermediate situation between the abraded and the mirror-like specimens. The last described characteristics depend mainly on the surface and microstructural peculiarities resulting from the rolling process.

关键词： AISI Type 444 sofc stacks Surface roughness Microstructure Surface finishing High-temperature oxidation

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：