Improvement of strength and ductility synergy in a room-temperature stretch-formable Mg-Al-Mn alloy sheet by twin-roll casting and low-temperature annealing

引用

Journal of Magnesium and Alloys 2022年第4期10卷 1066-1074页

作者： T.Nakata C.Xu K.Kaibe Y.Yoshida K.Yoshida S.Kamado Nagaoka University of Technology 1603-1KamitomiokaNagaoka 940-2188Japan School of Materials Science and Engineering Harbin Institute of Technology Harbin 150001China Sumitomo Electric Industries Ltd.1-1-1 KoyakitaItami 664-0016Japan

Strength and ductility synergy in an Mg-3mass%Al-Mn(AM30)alloy sheet was successfully improved via twin-roll casting and annealing at low-temperature.An AM30 alloy sheet produced by twin-roll casting,homogenization,hot-rolling,and subsequent annealing at 170℃ for 64 h exhibits a good 0.2%proof stress of 170 MPa and a large elongation to failure of 33.1%along the rolling direction.The sheet also shows in-plane isotropic tensile properties,and the 0.2%proof stress and elongation to failure along the transverse direction are 176 MPa and 35.5%,respectively.Though the sheet produced by direct-chill casting also shows moderate strengths if the annealing condition is same,the direct-chill casting leads to the deteriorated elongation to failure of 23.9%and 30.0%for the rolling and transverse directions,respectively.As well as such excellent tensile properties,a high room-temperature stretch formability with an Index Erichsen value of 8.3 mm could be obtained in the twin-roll cast sheet annealed at 170℃ for 64 h.The annealing at a higher temperature further improves the stretch formability;however,this results in the decrease of the tensile properties.Microstructure characterization reveals that the excellent combination of strengths,ductility,and stretch formability in the twin-roll cast sheet annealed at the low-temperature annealing is mainly attributed to the uniform recrystallized microstructure,fine grain size,and circular distribution of(0001)poles away from the normal direction of the sheet.

关键词： Magnesium Rolling Tensile property room temperature formability Twinning

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：