Highly transparent ytterbium doped yttrium lanthanum oxide ceramics

Journal of Rare Earths 2014年第3期32卷 254-258页

作者： M.Ivanov Yu.Kopylov V.Kravchenko 李江 A.Medvedev 潘裕柏 Institute of Electrophysics UrB of RAS 106Amundsena 620016 Ekaterinburg Russia Institute of Radioengineering and Electronics named after V.A. Kotelnikov RAS Vvedensky Sq. 1 Fryazino Moscow region 141120 Russia Shanghai Institute of ceramics Chinese Academy of Science Ural Federal University 19 Mira 620002 Ekaterinburg Russia

To prepare ytterbium doped lanthania yttria nanopowder a method of laser evaporation of mixed oxides was used. After calcinations of the powder at 1200 ℃ a pure single-phase solid solution yb3＋：（LaxY1-x）2O3 was formed in the nanoparticles. Influence of lanthanum oxide as an isovalent additive on the yttria structure was investigated. The lanthanium ions were proved to be a good aid to sinter yttria ceramics doped with Yb3＋ at moderate temperatures about 1650 ℃. The ceramics with relative density higher than 99.99% and grain size about 40 μm were fabricated. Full transmittance of 1.8 mm thick Yb0.11 La0.23Y1.66O3 ceramics reached 82.5% at 800 nm. This material could be a good gain medium for ytterbium high power pulse lasers.

关键词： re-doped ceramics nanopowders ytterbium oxide transparency

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：