Journal of Central South University 2015年第9期22卷 3302-3310页

作者： Jagannath Pal Satadal Ghorai Bikash Nandi Tapas Chakraborty Goutam Das T.Venugopalan CSIR-National Metallurgical Laboratory Tata Steel

Pelletization of hematite ore requires high fineness and very high induration temperature(~1325 °C) owing to its poor diffusion bonding unlike magnetite ore. Further, high-alumina hematite pellets show very high reduction degradation index(rdi) during low temperature(500-650 °C) reduction due to their volume expansion and lattice distortion. Noamundi(India) hematite ore contains very high Al2O3(2.3%) with adverse ratio of alumina to silica(~2) for which, it shows very high rdi. In this work, the acid pellets prepared from Noamundi ore fines of optimum Blaine fineness show good cold crushing strength(CCS). However, it shows very high rdi(77%). In order to reduce rdi, Mg O in form of two different gangue-containing fluxes, such as pyroxenite and olivine in varying quantities has been added. The optimum requirement and performance of these fluxes has been examined and compared. Both pyroxenite and olivine fluxed pellets show significant lowering of rdi(26% and 23%, respectively) and improvement of other properties, viz CCS, swelling indices etc with good reducibility(70%-77%). Finally, a good quality acidic hematite pellet was developed from high-alumina ore without using any lime which is very important charge material in combination of basic sinter in blast furnace.

关键词：铁矿球团冶金性能橄榄石辉石岩 MgO 酸性球团矿矿物 rdi

Effect of CaCl_2 on rdi and RI of Sinter

在线全文

学校读者我要写书评

暂无评论

Journal of Iron and Steel Research(International) 2010年第11期17卷 7-12页

作者： ZHANG Xu ZHANG Jian-liang HU Zheng-wen ZUO Hai-bin GUO Hong-wei School of Metallurgical and Ecological Engineering University of Science and Technology Beijing Beijing 100083 China

On the premise of maintaining the reducibility of sinter unchanged, it is of great significance to reduce the rdi （reduction degradation index） of sinter, which will improve the permeability of blast furnace burden column, so as to realize stable and smooth performance, and keep high yield and low consumption. Under laboratory conditions, a study on the rdi and RI （reduction index） of sinter was proposed, in which the sinter was immersed in solutions with different types and concentrations. In order to study the mechanism of CaCl2 effect on the rdi and RI of sinter, analysis based on the methods of IR spectra, SEM and chaleography was adopted. The results show that Cl^- is the main factor reducing the rdi of sinter, and the rdi and RI of sinter decrease with the increase of Cl^- concentration. With comprehensive consideration of the rdi and RI of sinter, when the concentration of Cl^ is 2%, the rdi of sinter will be significantly reduced and RI will not be affected.

关键词： sinter CaCl2 rdi RI

Effects of MgO Containing Additive on Low-Temperature Metallurgical Properties of Oxidized Pellet

在线全文

学校读者我要写书评

暂无评论

Journal of Iron and Steel Research(International) 2013年第7期20卷 25-28页

作者： GAO Qiang-jian SHEN Feng-man WEI Guo JIANG Xin ZHENG Hai-yan School of Materials and Metallurgy Northeastern University

As a main charging form of BF （blast furnace）, pellets play an important role in blast furnace process. However, comparing with sinters, pellets have many disadvantages, such as reduction swelling, low softening and melting temperature and so on. Therefore, the flux pellets have been applied in blast furnace widely, especially MgO containing pellets. The light burned magnesite is applied as MgO containing additive in pellet production. The char- acters of light burned magnesite are explored. Meanwhile, the effects of it on low-temperature metallurgical proper-ties are investigated such as low-temperature reduction degradation index （rdi）, compressive strength （CS） and the reduction swelling index （RSI）. The light burned magnesite calcined at 850 ℃ manifests better grindability, larger specific surface area, and higher hydration activity. It is found that the addition of light burned magnesite can im- prove low-temperature metallurgical properties （rdi, RSI） of the pellets. With the increase of light burned magne-site in pellets, the RSI and rdi decrease gradually; when the proportion of light burned magnesite does not exceed 2.0% in pellets, the CS decreases slightly, but it still surnasses 2689 N. which can still meet the demand of BF.

关键词： MgO containing additive pellet RSI rdi

在线全文

学校读者我要写书评

暂无评论

焦粉粒度对铁矿石烧结过程的影响

钢铁 2008年第10期43卷 8-12页

作者：欧大明孙骐沈红标阎丽娟石洪志必和必拓(BHP Billiton)纽卡斯尔技术中心必和必拓中国上海200020 宝钢股份公司技术中心上海201900 宝钢分公司制造部原料管理中心上海201900

铁矿石烧结中焦粉的燃烧过程取决于焦粉的粒度。通过烧结试验,研究了焦粉粒度对烧结性能和质量的影响(针对含10%MAC粉的配矿)。通过降低细焦粉粒级(<0.25 mm和<1 mm)的百分比来增加焦粉平均粒度,从而可以明显提高烧结速度、成品率和生产... 详细信息

铁矿石烧结中焦粉的燃烧过程取决于焦粉的粒度。通过烧结试验,研究了焦粉粒度对烧结性能和质量的影响(针对含10%MAC粉的配矿)。通过降低细焦粉粒级(rdi(还原粉化指数)改善。烧结矿矿相分析发现,即使用较粗焦粉的试验需要的燃料消耗率更低,但烧结成品包含的磁铁矿相更多,再生赤铁矿的含量更少。

关键词：铁矿石烧结焦粉粒度火焰前锋 rdi

在线全文

学校读者我要写书评

暂无评论

广西某高速沥青路面使用性能评价

江西建材 2023年第2期 326-328页

作者：李飞林广西壮族自治区高速公路发展中心广西南宁530000

文中采用CT616道路智能检测车、路面横向力系数测试车和激光动态弯沉测量系统,对广西某高速路面技术状况(PCI、RQI、rdi、SRI、PSSI、PQI等参数)进行了检测,结果表明,路面总体技术状况良好,行车道技术状况相对较差。文中最后给出了养护... 详细信息

文中采用CT616道路智能检测车、路面横向力系数测试车和激光动态弯沉测量系统,对广西某高速路面技术状况(PCI、RQI、rdi、SRI、PSSI、PQI等参数)进行了检测,结果表明,路面总体技术状况良好,行车道技术状况相对较差。文中最后给出了养护建议。

关键词：沥青路面道路智能检测车 RQI PCI rdi PSSI PQI

在线全文

学校读者我要写书评

暂无评论

MgO含量对烧结矿质量的影响

南钢科技与管理 2022年第4期 14-17页

作者：明廷流李博居鹤鸣炼铁事业部

随着原料的结构和工艺条件的变化,烧结矿MgO的最佳含量范围也会跟着变化。现有研究结果表明,烧结矿最佳Mg0的含量为1.8%~2.0%。在此基础上我们通过烧结杯试验,进一步缩小烧结矿Mg0的含量控制范围为1.8%~1.9%,烧结生产过程参数得到了优化... 详细信息

随着原料的结构和工艺条件的变化,烧结矿MgO的最佳含量范围也会跟着变化。现有研究结果表明,烧结矿最佳Mg0的含量为1.8%~2.0%。在此基础上我们通过烧结杯试验,进一步缩小烧结矿Mg0的含量控制范围为1.8%~1.9%,烧结生产过程参数得到了优化,烧结矿的性能有所提高,更能满足高炉治炼的要求。

关键词：烧结矿 MgO含量烧结速度转鼓指数 rdi 熔滴性能

维普期刊数据库评论

在线全文

维普期刊数据库

学校读者我要写书评

暂无评论

普矿配加对钒钛烧结矿质量的影响

钢铁 2015年第8期50卷 10-15页

作者：周密姜涛杨松陶王艳军张立恒薛向欣东北大学材料与冶金学院辽宁沈阳110819

通过烧结杯制备了全钒钛以及配加一定量印粉(YD)、马粉(MF)及自产普粉(ZF)的钒钛烧结矿,并对其烧结速度、烧损率、成品率、转鼓强度、rdi>3.15 mm以及软化性质进行了测定及分析。试验结果表明:全钒钛烧结矿质量较差,尤其是rdi>3.15 mm过... 详细信息

通过烧结杯制备了全钒钛以及配加一定量印粉(YD)、马粉(MF)及自产普粉(ZF)的钒钛烧结矿,并对其烧结速度、烧损率、成品率、转鼓强度、rdi>3.15 mm以及软化性质进行了测定及分析。试验结果表明:全钒钛烧结矿质量较差,尤其是rdi>3.15 mm过低,产率较低,需配加普矿提高其质量及产量。选择普粉时应兼顾其制粒性以及化学成分等,应保证烧结矿中一定量的SiO2、MgO以及Al2O3不宜过高。配加3种普粉均有利于提高烧结速度及提高软化区间,配加自产粉有利于提高钒钛烧结矿的转鼓强度(64.25%)以及rdi>3.15 mm,但降低了成品率;配加印粉有利于提高转鼓强度、成品率,但是降低了rdi>3.15 mm;配加马粉有利于提高强度和rdi>3.15 mm,但是其铁品位低、烧损大。配加13%(印粉+马粉+自产)钒钛烧结矿的指标优于配加6.5%(印粉+马粉+自产)的钒钛烧结矿。

关键词：钒钛粉烧结强度 rdi 铁矿粉

在线全文

学校读者我要写书评

暂无评论

提高烧结矿rdi性能工艺模型研究

山西冶金 2023年第1期46卷 75-76页

作者：苗慧源福建三宝钢铁有限公司福建漳州363000

研究了一种提高烧结矿rdi性能的方法,通过建立原材料中铁矿硬度、强度和纯度值与烧结矿的低温还原粉化指数rdi的函数关系,确定铁矿加入含量,通过调整石灰石含量调整原料碱度以及烧结温度。

关键词： rdi 烧结矿铁矿硬度碱度烧结温度

气候变化与人类活动对内蒙古东部草地净初级生产力的影响

在线全文

学校读者我要写书评

暂无评论

生态学报 2020年第19期40卷 6912-6924页

作者：欧阳玲马会瑶王宗明王昭伟于显双赤峰学院赤峰024000 海图信息中心天津300000 中国科学院东北地理与农业生态研究所长春130102 国家地球系统科学数据中心北京100101 赤峰生态环境监测站赤峰024000

内蒙古东部草地是该区域的主体生态系统类型,属于脆弱的生态系统,对气候和人类活动反应敏感。基于土地覆被数据和改进CACS模型,估算得到的草地NPP,分析2000—2015年内蒙古东部草地和NPP时空格局与年际动态。进而,定义相对退化指数(rdi)... 详细信息

内蒙古东部草地是该区域的主体生态系统类型,属于脆弱的生态系统,对气候和人类活动反应敏感。基于土地覆被数据和改进CACS模型,估算得到的草地NPP,分析2000—2015年内蒙古东部草地和NPP时空格局与年际动态。进而,定义相对退化指数(rdi),确定草地生产力变化过程中人类活动因素的贡献率,分析内蒙古东部地区2000—2015年rdi空间格局与年际动态。同时,分析16年间NPP和气候因子相关关系。结果表明:1)2000—2015年间,损失草地面积4743.80 km^2,新增草地面积2705.57 km^2。2)2000—2015年内蒙古东部地区草地植被平均NPP位于166.56—248.14 gC m-2 a-1之间,NPP在波动中呈现明显的上升趋势(3.65 gC m-2 a-1/a,R2=0.47)。3)2000—2015年rdi在16.64%—30.54%之间波动,rdi值呈缓慢下降趋势,表明人类活动对草地植被净初级生产力的干扰程度在下降。4)草地NPP变化主要是因为草地本身生产力下降。整体来看相关草地保护工作取得了阶段性进展,草地生境质量得到有效缓解,草地生态环境得到转变。

关键词：内蒙古东部 NPP rdi 气候变化草地

深度视电阻率成像在航空瞬变电磁法探测矿体的研究及应用

在线全文

学校读者我要写书评

暂无评论

地球物理学进展 2018年第4期33卷 1707-1712页

作者：王笠洁龚育龄杨海燕骆燕王培建东华理工大学地球物理与测控技术学院南昌330013 核工业航测遥感中心石家庄050002 铀资源地球物理勘查技术中心重点实验室石家庄050002

深度视电阻率成像是航空瞬变电磁法中数据处理及分析的重要过程,能够提供具有参考价值的导体深度、垂向延伸等信息,并能准确提供每条航空瞬变电磁测量系统测线上的一维层状介质视导电率结构断面.而航空瞬变电磁法作为一种先进的地球物... 详细信息

深度视电阻率成像是航空瞬变电磁法中数据处理及分析的重要过程,能够提供具有参考价值的导体深度、垂向延伸等信息,并能准确提供每条航空瞬变电磁测量系统测线上的一维层状介质视导电率结构断面.而航空瞬变电磁法作为一种先进的地球物理勘探技术,近年来在国外多金属矿产勘查中应用效果显著.本文简要介绍了视电阻率的分析处理方法,以几组不同导体的MAXWELL板状模型为例,计算一维视电阻率深度,得到直观的视电阻率深度成像图.此项技术首次在黄土坡矿床开展测量试验的处理中,获得良好的效果,加快了航空瞬变电磁法的处理工作进程.

关键词：航空瞬变电磁法 rdi 视电阻率新疆黄土坡