Low temperature molten salt synthesis of porous La_(1-x)Sr_xMn_(0.8)Fe_(0.2)O_3(0≤x≤0.6) microspheres with high catalytic activity for CO oxidation

引用

Chinese Journal of Catalysis 2016年第8期37卷 1431-1439页

作者：黄学辉牛鹏举商晓辉武汉理工大学材料科学与工程学院湖北武汉430070

A molten salt method was developed to prepare porous La1‐xSrxMn0.8Fe0.2O3 （0≤ x ≤ 0.6） micro‐spheres using hierarchical porous δ‐MnO2 microspheres as a template in eutectic NaNO3‐KNO3. X‐ray diffraction patterns showed that single phase LaMn0.8Fe0.2O3 with good crystallinity was syn‐thesized at 450℃ after 4 h. Transmission electron microscope images exhibited that the LaMn0.8Fe0.2O3 sample obtained at 450？？ after 4 h possessed a porous spherical morphology com‐posed of aggregated nanocrystallites. Field emission scanning electron microscope images indicated that the growth of the porous LaMn0.8Fe0.2O3 microspheres has two stages. SEM pictures showed that a higher calcination temperature than 450？？ had an adverse effect on the formation of a po‐rous spherical structure. The LaMn0.8Fe0.2O3 sample obtained at 450？？ after 4 h displayed a high BET surface area of 55.73 m2/g with a pore size of 9.38 nm. Fourier transform infrared spectra suggested that Sr2＋ions entered the A sites and induced a decrease of the binding energy between Mn and O. The CO conversion with the La1‐xSrxMn0.8Fe0.2O3 （0≤x≤0.6） samples indicated that the La0.4Sr0.6Mn0.8Fe0.2O3 sample had the best catalytic activity and stability. Further analysis by X‐ray photoelectron spectroscopy demonstrated that Sr2＋doping altered the content of Mn4＋ions, oxygen vacancies and adsorbed oxygen species on the surface, which affected the catalytic performance for CO oxidation.

关键词： Molten salt method δ-MnO2 microsphere porous spherical structure Calcination temperature Carbon monoxide oxidation

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

porous spherical NiO@NiMoO4@PPy nanoarchitectures as advanced electrochemical pseudocapacitor materials

引用

Science Bulletin 2020年第7期65卷 546-556,M0004页

作者： Ting-Feng Yi Li-Ying Qiu Jie Mei Si-Yu Qi Ping Cui Shaohua Luo Yan-Rong Zhu Ying Xie Yan-Bing He School of Materials Science and Engineering Northeastern UniversityShenyang 110819China Key Laboratory of Functional Inorganic Material Chemistry Ministry of EducationSchool of Chemistry and Materials ScienceHeilongjiang UniversityHarbin 150080China Shenzhen Geim Graphene Center Tsinghua Shenzhen International Graduate SchoolTsinghua UniversityShenzhen 518055China School of Chemistry and Chemical Engineering Anhui University of TechnologyMaanshan 243002China School of Resources and Materials Northeastern University at QinhuangdaoQinhuangdao 066004China Key Laboratory of Dielectric and Electrolyte Functional Material Hebei Province Qinhuangdao 066004China

In this work, a rational design and construction of porous spherical Ni O@NiMoO4 wrapped with PPy was reported for the application of high-performance supercapacitor(SC). The results show that the NiMoO4 modification changes the morphology of Ni O, and the hollow internal morphology combined with porous outer shell of Ni O@NiMoO4 and Ni O@NiMoO4@PPy hybrids shows an increased specific surface area(SSA), and then promotes the transfer of ions and electrons. The shell of NiMoO4 and PPy with high electronic conductivity decreases the charge-transfer reaction resistance of Ni O, and then improves the electrochemical kinetics of Ni O. At 20 Ag^-1, the initial capacitances of Ni O, NiMoO4, Ni O@NiMoO4 and Ni O@NiMoO4@PPy are 456.0, 803.2, 764.4 and 941.6 Fg^-1, respectively. After 10,000 cycles, the corresponding capacitances are 346.8, 510.8, 641.2 and 904.8 Fg^-1, respectively. Especially, the initial capacitance of Ni O@NiMoO4@PPy is 850.2 Fg^-1, and remains 655.2 Fg^-1 with a high retention of 77.1% at30 Ag^-1 even after 30,000 cycles. The calculation result based on density function theory shows that the much stronger Mo-O bonds are crucial for stabilizing the Ni O@NiMoO4 composite, resulting in a good cycling stability of these materials.

关键词： NiO NiO@NiMoO4@PPy porous spherical structure Supercapacitor Cycling stability

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：