Controlled Growth Morphology of porous Nanocrystal iron oxide by Electrodeposition

Chemical Research in Chinese Universities 2009年第5期25卷 595-599页

作者： LI Li SHI Ke-ying Key Laboratory of Functional Inorganic Material Chemistry Ministry of Education Laboratory of Physical Chemistry School of Chemistry and Materials Science Heilongjiang University Harbin 150080 P. R. China

Fe（Ⅱ） was deposited into the bottom of the mesopores of highly ordered large caged cubic mesoporous silica by electrodeposition. And the deposited Fe mesoporous silica thin film was treated by 1%---4% HF to remove the SiO2 template and then calcined. It was found that nanowire bundles, dendritic plates of porous iron oxide, dense parallel backbones of porous iron oxide were obtained at -1.4-- -1.6 V and 0.08--0.1 mol/L electrolyte concentration after calcinations; the dendritic pattern of porous iron oxide film templated by the SBA-16 film was obtained in macrostructure at a higher absolute value of cathode potential（-1.7-- -1.8 V） and a lower electrolyte concentration（0.02-0.05 mol/L）, the dendritic pattern of porous iron oxide film could copy the microstructure of SBA-16 film; Fe（II） nanowires grew and formed in one dimension（1D） and two-dimension（2D） electrocrystallization at a potential of-l.6-- -1.7 V and an electrolyte concentration of 0.05 mol/L, and the shape of the ID or 2D crystalline iron oxide nanowires calcined was similar to the original shape of the SBA-16 channels. The desired morphology and size of porous nanocrystal iron oxide can be obtained by adjusting the applied potential value and electrolyte concentration, and all kinds of morphologies of porous nanostructure crystal iron oxide can be prepared.

关键词： Electrocrystallization Deposition porous iron oxide Morohology

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：