Preparation and characterization of carbon nano-sheet powders

Petroleum Science 2008年第1期5卷 79-82页

作者： Yang Wubao Zhao Zhen Fang Songhua Wang Yong Yang Size Lin Li School of Electromechanical Engineering China University of Petroleum Beijing 102249 China School of chemical Science and Engineering China University of Petroleum Beijing 102249 China Institute of Physics Chinese Academy of Sciences Beijing 100080 China

Carbon nanosheet films were deposited on A1 substrates by using plasma assisted chemical vapor deposition （PACVD） technique. And after being peeled off from A1 substrates, carbon nanosheet powders （CNSPs） were obtained. In Raman spectrum of carbon film, there was a strong and broadened peak at about 1,580 cm^-1, indicating a carbon diamond-like film. Atomic force microscope image showed that the carbon diamond-like film had a grain size less than 100 nm, and its surface roughness Ra was 17.95 nm in an area of 5×5 μm^2. The CNSPs were irregular sheets with curly edges and a length of several micrometers to several hundreds of micrometers. The BET surface area of CNSPs was 6.66 m^2/g with no micro-pore present, which was confirmed by N2 adsorption-desorption characterization. In the adsorption testing, when the relative pressure p/po was higher than 0.3, the adsorption behavior did not follow the Langmuir equation. The addition of CNSPs to carbon black （catalyst support） could improve hydrodesulfurization performance of carbon supported Ni-W catalysts for diesel oil.

关键词： plasma assisted chemical vapor deposition carbon nanosheet powder N2 adsorption/desorption hydrodesulfurization

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：