Effect of edge cracks on critical current degradation in REBCO tapes under tensile stress

Superconductivity 2022年第1期1卷 52-62页

作者： Zhirong Yang Yi Li Peng Song Mingzhi Guan Feng Feng Timing Qu State Key Laboratory of Tribology Department of Mechanical EngineeringTsinghua UniversityBeijing 100084China Department of Mechanical Engineering Advanced Manufacturing InstituteTexas Center for SuperconductivityUniversity of HoustonHoustonTX 77024USA Institute of Modern Physics Chinese Academy of SciencesLanzhou 730000China Lab of Intelligent Manufacturing and Precision Machining Tsinghua Shenzhen International Graduate SchoolTsinghua UniversityShenzhen 518055China

The slitting process for manufacturing REBa2Cu3O7δ(REBCO,RE=Rare earth)tapes of required width significantly improves the production efficiency and reduces production costs.However,edge cracks induced by the slitting process of wide REBCO tapes may cause premature degradation under high tensile stress in highfield magnets.Therefore,it is necessary to evaluate the effect of edge cracks of REBCO tapes on the critical current(Ic)degradation.Firstly,Ic degradation under artificial cracks was measured to validate the applicability of linear elastic fracture mechanics for the REBCO layer.The maximum circumferential stress criterion was used to derive the mixed-mode stress intensity factor of multiple oblique edge cracks.A semi-analytical model considering edge crack properties such as angleβ,spacing d,and length a,was built to evaluate the critical load and critical crack.We found that when the stress intensity factor at the crack tip is below KIC?2:3 MPa ffiffiffiffim p,edge cracks did not propagate.We examined commercial REBCO tapes manufactured by two different processes,concluding that edge cracks in these tapes will not cause premature degradation.

关键词： REBCO Degradation Stress intensity factor multiple oblique edge cracks Fracture toughness

来源：

维普期刊数据库评论

在线全文

维普期刊数据库

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：