microstructure and mechanical behaviour of proton-and ion-irradiated ll_2 intermetallic compounds

Journal of Materials Science & Technology 1994年第4期10卷 235-245页

作者： F. C. Chen and A .J.Ardell (Dept. of Materials Science and Engineering, University of California, Los Angeles, CA 90024-1595, USA) Univ of California Los Angeles United States

The results of mechanical testing and transmission electron microscopy on the ordered intermetallic ll2 compounds1Zr3Al, Ni3Al, Ni3Si and Ni3Ge after irradiation with protons or heavy ions at high or low tem peratu re are presented and discussed. Using a minjaturjzed disk-bend test. it was found that proton irradiation of Zr3Al. Ni3Al and Ni3Si raises their yield strength :a single test of Ni3Ge shows no effect on the fracture stress of this brittle intermetallic The Vickers microhardness of all four alloys is raised by proton irradiation. The irradiations cause all the alloys to disorder. the extent of which is dependent on irradiation temperature Microstructural defects are produced by the irradiations Some exhibit strain-field contrast under dynamic two-beam diffracting conditions. Other distinct defect clusters are imaged only in dark-field using su perlattice reflections, These latter defects are discussed in the context of current arnorphization models. The strength increase of Zr3Al, Ni3Al and Ni3Si is attributed to a combination of disordering and strengthening from defects. The lack of an effect of irradiation on the fracture stress of Ni3Ge. in which voids were observed, requires further experiments

关键词： Ni Si Zr microstructure and mechanical behaviour of proton-and ion-irradiated ll2 intermetallic compounds Figure

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：