Effects of Loading Rate on Flexural-tension Properties and Uniaxial Compressive Strength of micro-surfacing Mixture

Journal of Wuhan University of Technology(Materials Science) 2010年第4期25卷 656-658页

作者：陈筝 School of Materials Science & Engineering Xi'an University of Architecture & Technology

The major objective of this research was to discuss the effects of loading rate on the flexural-tension properties and uniaxial compressive strength of micro-surfacing mixture using three-point bending test and uniaxial compressive test respectively. As a preventive maintenance surface treatment on asphalt pavement, micro-surfacing was formed on the basis of the ISSA recommendation of an optimum micro-surfacing design. Tests were conducted over a wide range of temperature to investigate the difference of properties from low loading rate to a relatively high loading rate. Three-point bending test was used to study the flexural strength, strain and modulus of micro-surfacing mixture, and uniaxial compressive test was carried out to obtain the relationship between strength and the loading rate as well as temperature. The experimental results showed that flexural strength at high loading rate was larger than that at low loading rate. The flexural strength difference between low and high loading rate enlarged when the temperature rose. The flexural strain at high loading rate increased compared with results of the low loading rate. Results of the flexural modulus revealed that micro-surfacing mixture exhibited better anti-cracking characteristic at low temperature when given a relatively low loading rate. Results of uniaxial compressive test revealed that the strength difference of micro-surfacing among different loading rates increased with the increase of temperature. The logarithm relationship between the strength and loading rate over a wide range of temperature was obtained to compare the experimental and predicted values, which resulting in a reasonable consistency.

关键词： loading rate flexural-tension properties uniaxial compressive strength micro-surfacing

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

Rutting Resistance of HMA Rehabilitated with micro-surfacing

引用

Open Journal of Civil Engineering 2018年第2期8卷 245-255页

作者： Arbia Garfa Alan Carter Anne Dony école de Technologie Supérieure ETS Montréal Canada Ecole Spécial des travaux publics ESTP Paris France

The work presented here is a study on the measurement and prediction of the rutting resistance of previously rutted asphalt mixes rehabilitated with a layer of micro-surfacing manufactured with virgin and recycled aggregates at different stages of aging. The experimental procedure consisted of rutting tests on hot mix asphalt slabs already degraded and repaired with virgin and recycled micro-surfacing. Then, the evolution of the behavior of micro-surfacing cast on the hot mix asphalt slabs is observed according to loading cycles of the pavement rutting tester MLPC. Before rutting tests, slabs are subjected to 24 hours at 50°C and aged for 2 days and 5 days at 85°C in the oven. The results showed rutting percentages of 6.3% for hot mix asphalt slabs aged for 2 days and 7.2% for 5 days. These hot mix slabs repaired with virgin micro-surfacing have rutting percentage of about 9.2 % for 2 days of aging and 6.5% for 5 days of aging. While, the HMA slabs repaired with recycled micro-surfacing have rutting percentage of about 8.1% for 2 days of aging and 5.9% for 5 days of aging. These results allowed the development of a prediction model based essentially on three predictor variables including cycle number, rutting state and percentage of water in the micro-surfacing material. The developed model shows a strong correlation between the predicted rutting values and the rutting values measured with the MLPC rut tester. Thermal aging in oven has a positive impact on the resistance to permanent deformation of new asphalt mixes and those rehabilitated with micro-surfacing. The parameters of rutting state and contribution water are significant in the rutting prediction model, while the cycle number remains a non-significant parameter in the model but determinant.

关键词： HMA RAP micro-surfacing Rutting Aging

来源：

维普期刊数据库评论

在线全文

维普期刊数据库

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：