Microstructure and mechanical properties of an mg-4.0sm-1.0ca alloy during thermomechanical treatment

Journal of Rare Earths 2016年第11期34卷 1134-1138页

作者：罗小萍房大庆李秋书柴跃生 College of Materials Science and Engineering Taiyuan University of Science and Technology

The microstructure and mechanical properties of an as-cast mg-4.0sm-1.0ca alloy were investigated during thermome-chanical treatments consisting of hot extrusion, rolling, and aging at 473 K. mg41sm5 phases containing ca and needle-like mg2ca phases formed in the mg matrix, and the average grain size and elongation were 4.2μm and 27%, respectively, after hot extrusion, which implied an increase in ductility. In addition, after the rolling, the grain size was further refined, and the tensile strength in-creased to 293 MPa. A new precipitate mg3sm was found in the peak-aged mg-4.0sm-1.0ca alloy and this alloy displayed the best mechanical properties, with a peak hardness of 83 HV and ultimate tensile strength of 313 MPa; these properties were attributed to grain refinement strengthening, solid solution strengthening, work hardening, and precipitation strengthening.

关键词： mg-sm-ca alloy thermomechanical treatment microstructure mechanical properties rare earths

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：