Mechanism of pore formation and structural characterization for mesoporous mg-al composite oxides

在线全文

学校读者我要写书评

暂无评论

Science China Chemistry 2002年第1期45卷 37-45页

作者：赵芸矫庆泽段雪 1. Key Laboratory of Science and Technology of Controllable Chemical Reactions Ministry of Education Beijing Uni-versity of Chemical Technology 100029 Beijing China

mg-al layered double hydroxides (LDH) with different particle sizes were prepared using different aging times at high supersaturation by a new method developed in our laboratory. The key features of this method are a very rapid mixing and nucleation process followed by a separate aging process. By calcination of LDH at 500°C, mesoporous mg-al composite oxides with an extremely narrow pore size distribution were produced. The crystal structure of the mg-al composite oxides was a multiphasic one consisting of mgO-like crystals and a layered material.

关键词： layered double hydroxide mg-al composite oxide mesopore crystal structure.

添加Ni箔中间层的mg-al扩散焊接接头界面结构和力学性能

在线全文

学校读者我要写书评

暂无评论

材料工程 2015年第1期43卷 13-17页

作者：张建罗国强沈强黄治军武汉钢铁(集团)公司研究院武汉430080 武汉理工大学材料复合新技术国家重点实验室武汉430070 华中科技大学材料科学与工程学院武汉430074

采用扩散焊接工艺,通过添加Ni箔中间层对镁铝异种金属进行焊接。利用无损检测、电子探针、扫描电镜、万能材料试验机研究了mg/Ni/al焊接接头界面的组织结构和力学性能。结果表明:Ni箔中间层可以有效阻止界面处mg,al元素的相互扩散,接头... 详细信息

采用扩散焊接工艺,通过添加Ni箔中间层对镁铝异种金属进行焊接。利用无损检测、电子探针、扫描电镜、万能材料试验机研究了mg/Ni/al焊接接头界面的组织结构和力学性能。结果表明:Ni箔中间层可以有效阻止界面处mg,al元素的相互扩散,接头界面处没有生成mg-al金属间化合物。在焊接温度440℃,保温时间90min时,接头抗剪强度达到最大值20.5MPa。mg/Ni/al接头由al,Ni和mg,Ni的相互扩散形成,接头界面形成al-Ni过渡区和mg-Ni过渡区,界面主要物相分别为al3Ni2,al3Ni和mg2Ni,过渡区厚度随焊接温度升高而增加。

关键词： mg-al Ni箔扩散焊显微结构

mg-al水滑石的制备及对水中氟离子的吸附效果研究

在线全文

学校读者我要写书评

暂无评论

功能材料 2024年第4期55卷 4179-4184,4200页

作者：邹志鑫李敏任晓影刘佳惠焦桂萍赵瀛中国船舶集团有限公司第七一八研究所河北邯郸056000

通过共沉淀法制备了mg-al水滑石,研究了镁铝摩尔比对mg-al水滑石的晶格结构、微观形貌、光谱性能的影响。以NaF溶液为模拟含氟废水,测试了mg-al水滑石对水中氟离子的吸附量和去除率,通过吸附模型研究了相应的吸附过程和机理。结果表明,M... 详细信息

通过共沉淀法制备了mg-al水滑石,研究了镁铝摩尔比对mg-al水滑石的晶格结构、微观形貌、光谱性能的影响。以NaF溶液为模拟含氟废水,测试了mg-al水滑石对水中氟离子的吸附量和去除率,通过吸附模型研究了相应的吸附过程和机理。结果表明,mg-al水滑石外观为片层状结构,片层之间相互交叉堆积,镁铝比增大时,mg-al水滑石的层间距增大。水滑石对氟离子的饱和吸附量和去除率随着镁铝比的增大表现出先增大后减小的趋势,在吸附80 min时吸附量接近饱和,3mg-al水滑石的饱和吸附量达到最大值43.16 mg/g,去除率在120 min时达到最大值90.5%,经过5次吸附再生循环使用后,3mg-al水滑石对氟离子的去除率降至69.4%,保持率达到76.69%,具有良好的可重复利用性能。通过对mg-al水滑石吸附氟离子的数据进行拟合,发现mg-al水滑石吸附氟离子的过程更符合准二级动力学模型,主要以化学吸附作用为主。

关键词： mg-al 水滑石共沉淀法氟离子再生循环吸附动力学

mg-al CLDHs/H_2O_2体系降解结晶紫染料废水的研究

在线全文

学校读者我要写书评

暂无评论

硅酸盐通报 2015年第5期34卷 1223-1228页

作者：郭效军李海如李雨甜西北师范大学化学化工学院兰州730070

以mg-alCLDHs(Calcined mg-al layered double hydroxide)和H2O2组成的类芬顿体系催化降解结晶紫(Crystal violet,CV)染料废水。考察了p H值、催化剂用量、氧化剂用量、染料起始浓度、反应温度、反应时间等因素的影响,并对mg-al CLDHs... 详细信息

以mg-alCLDHs(Calcined mg-al layered double hydroxide)和H2O2组成的类芬顿体系催化降解结晶紫(Crystal violet,CV)染料废水。考察了p H值、催化剂用量、氧化剂用量、染料起始浓度、反应温度、反应时间等因素的影响,并对mg-al CLDHs催化剂的再生能力进行了测试。结果表明:对浓度为40 mg/L的结晶紫溶液,当mg-al CLDHs用量为0.005 g,H2O2用量为1 m L,p H为7.0,降解温度为35℃,反应时间为15 min,结晶紫脱色率98%以上,催化剂再生性良好。动力学研究表明该反应符合一级动力学模型,35℃时速率常数为0.28 min-1,表观活化能为46.03 k J·mol-1。

关键词： mg-al CLDHs H2O2 类芬顿反应结晶紫降解

Microstructure and properties of mg-al binary alloys

在线全文

学校读者我要写书评

暂无评论

China Foundry 2006年第4期3卷 270-274页

作者： ZHENG Wei-chao LI Shuang-shou TANG Bin ZENG Da-ben Fundamental Industry Training Center Department of Mechanical Engineering Fundamental Industry Training Center Department of Engineering Mechanics Tsinghua University Beijing 100084 China Department of Mechanical Engineering

The effects of different amounts of added al, ranging from 1 % to 9 %, on the microstructure and properties of mg-al binary alloys were investigated. The results showed that when the amount of added al is less than 5%, the grain size of the mg-al binary alloys decreases dramatically from 3 097 μm to 151 μm with increasing addition of al. Further addition of al up to 9% makes the grain size decrease slowly to 111 μm. The α-mg dendrite arms are also refined. Increasing the amount of added al decreases the hot cracking susceptibility of the mg-al binary alloys remarkably, and enhances the micro-hardness of the α-mg matrix.

关键词： mg-al binary alloys grain size α-mg dendrite eutectic microstructure hot cracking

稀土元素Y和Gd对mg-al系压铸镁合金组织和性能的影响

在线全文

学校读者我要写书评

暂无评论

稀土元素Y和Gd对Mg-Al系压铸镁合金组织和性能的影响

作者：代丽沈阳工业大学

学位级别：硕士

mg-al系镁合金是目前应用非常广泛的合金系，具有优良的压铸工艺性能，适合压铸生产，其强度也越来越得到工业领域的重视。稀土元素被认为可细化晶粒、提高镁合金的力学性能。因此，研究稀土元素Y和Gd对压铸mg-al系镁合金显微组织和力... 详细信息

mg-al系镁合金是目前应用非常广泛的合金系，具有优良的压铸工艺性能，适合压铸生产，其强度也越来越得到工业领域的重视。稀土元素被认为可细化晶粒、提高镁合金的力学性能。因此，研究稀土元素Y和Gd对压铸mg-al系镁合金显微组织和力学性能的影响，寻求更高强度的mg-al系镁合金，有利于镁合金在工业生产中的广泛应用，具有实际意义。本文通过显微组织观察、X-射线衍射分析、拉伸性能测试以及低周疲劳试验，对压铸态和时效态mg-5al-xGd镁合金的性能进行了测试与分析，以探讨稀土元素对mg-5al-xGd镁合金组织和性能的影响，并研究了不同热处理状态下的铸造mg-4al-2Y镁合金的显微组织和拉伸性能。显微组织观察表明：提高压铸态和时效态mg-5al-xGd镁合金中Gd的含量，可使合金的显微组织发生细化，β-mg17al12相由连续网状分布演化成断续网状分布，共晶组织数量减少，但稀土化合物相发生粗化。时效处理和固溶+时效处理可使mg-4al-2Y合金晶粒尺寸更均匀，并促进第二相在晶界析出。拉伸性能测试表明：时效处理可提高mg-5al-xGd合金的拉伸性能，且随着Gd含量增加，压铸态和时效态合金的抗拉强度和屈服强度均呈现先提高后降低的趋势，其中Gd含量为2%的时效态mg-5al-2Gd合金具有最高的强度。时效处理以及固溶+时效处理可提高铸态mg-4al-2Y镁合金的抗拉强度，且时效处理效果更显著。mg-5al-xGd合金与mg-4al-2Y合金的拉伸断口形貌观察均可见大量韧窝和解理台阶，合金表现为韧性-脆性混合断裂特征。疲劳试验结果表明：在总应变幅控制的低周疲劳条件下，压铸态和时效态mg-5al-xGd镁合金均表现为循环应变硬化和循环稳定，且时效处理可提高mg-5al-xGd合金的循环变形抗力。Gd含量为1%、2%时的循环变形抗力均高于Gd含量为3%时的循环变形抗力。疲劳断口形貌分析表明：在给定的外加总应变幅下，压铸态和时效态mg-5al-xGd镁合金的疲劳裂纹以穿晶方式萌生于试样表面并以穿晶方式扩展。

关键词： mg-al 合金显微组织力学性能低周疲劳稀土元素Y 稀土元素Gd

新型al-C晶粒细化剂的制备及对mg-al合金显微组织的影响研究

同方学位论文库评论

在线全文

同方学位论文库

学校读者我要写书评

暂无评论

汽车工艺与材料 2024年第7期 40-44页

作者：李雨乐张爱民兖利鹏郑炀婧黄娟河南工学院材料科学与工程学院新乡453003

采用原位反应烧结法制备了新型al-5C中间合金,利用光学显微镜(OM)、X射线衍射(XRD)和扫描电子显微镜(SEM)等研究了制备工艺对al-5C中间合金组织以及该中间合金对mg-al合金晶粒细化的影响。结果表明,原位反应烧结法改善了al与C的润湿性,A... 详细信息

采用原位反应烧结法制备了新型al-5C中间合金,利用光学显微镜(OM)、X射线衍射(XRD)和扫描电子显微镜(SEM)等研究了制备工艺对al-5C中间合金组织以及该中间合金对mg-al合金晶粒细化的影响。结果表明,原位反应烧结法改善了al与C的润湿性,al-C的反应程度与球磨时间、烧结温度、烧结时间和压块方式有关;延长球磨时间、提高烧结温度或适当延长烧结时间均能促进al-C反应,生成细小的al4C3颗粒;al-5C中间合金能有效地细化mg-3al合金的组织,添加量(质量分数)为2%时晶粒细化效果最佳。

关键词： mg-al 合金晶粒细化 al-C 细化剂原位合成

维普期刊数据库博看期刊

MoO3、V2O5、CdO与mg－al混合物的热特性

在线全文

学校读者我要写书评

暂无评论

火工情报 1999年第3期 35-42页

作者：古贺道生杜力等

焙烧层状氢氧化镁铝对水溶液中As(Ⅲ)和As(Ⅴ)的吸附性能比较

维普期刊数据库评论

在线全文

维普期刊数据库

学校读者我要写书评

暂无评论

环境科学 2009年第3期30卷 748-754页

作者：邢坤王海增李晓玉中国海洋大学化学化工学院海洋化学理论与工程技术教育部重点实验室青岛266100

通过静态吸附实验,对比研究了焙烧层状氢氧化镁铝（mg-al CLDH）对水溶液中As（Ⅲ）和As（Ⅴ）阴离子的吸附特性,并用粉末X射线衍射对mg-al CLDH吸附前后的结构进行了表征.结果表明,mg-al CLDH对As（Ⅲ）和As（Ⅴ）的吸附是通过“结构... 详细信息

通过静态吸附实验,对比研究了焙烧层状氢氧化镁铝（mg-al CLDH）对水溶液中As（Ⅲ）和As（Ⅴ）阴离子的吸附特性,并用粉末X射线衍射对mg-al CLDH吸附前后的结构进行了表征.结果表明,mg-al CLDH对As（Ⅲ）和As（Ⅴ）的吸附是通过“结构记忆”效应实现的.mg-al CLDH可有效脱除溶液中的含砷阴离子,其吸附量明显高于现有文献的报道.当As（Ⅲ）和As（Ⅴ）初始浓度（以As计）分别高达10 mg.L-1和40 mg.L-1时,吸附后溶液中残余As浓度〈10μg.L-1.在本研究的初始浓度4～500mg.L-1范围内,在298～323 K下,As（Ⅲ）和As（Ⅴ）在mg-al CLDH上的最大吸附量（以As计）分别为150.46～224.03 mg.g-1和149.62～224.76 mg.g-1,且吸附量仍呈直线上升趋势.吸附量随温度升高而增大,表现为吸热吸附.As（Ⅲ）和As（Ⅴ）阴离子在mg-al CLDH上的吸附等温线分别属于L型和H型.在低浓度区域,As（Ⅲ）在mg-al CLDH上的吸附可用Freundlich等温方程式来描述,As（Ⅴ）更符合Langmuir等温方程式;在高浓度范围内,均可用Freundlich等温方程式来描述.在相同初始浓度和温度下,mg-al CLDH对As（Ⅴ）的吸附速率和脱除率远远大于As（Ⅲ）,吸附速率和脱除率随溶液初始浓度的降低和温度的升高而增大,伪二级动力学方程可较好地描述二者在mg-al CLDH上的吸附动力学过程.吸附基本不受溶液初始pH值（3.0～10.0）和离子强度的影响.当溶液中As（Ⅴ）和As（Ⅲ）同时存在时,mg-al CLDH优先吸附As（Ⅴ）.

关键词： mg-al CLDH As(Ⅲ)阴离子 As(Ⅴ)阴离子吸附