Carbides Formation in marm247 Directional Solidified during Stress-Rupture Test at High Temperature

Journal of Minerals and Materials Characterization and Engineering 2023年第5期11卷 131-142页

作者： Daniel Moreno Itzik Mizrahi Yuri Lipkin Vasiliy Zevin Elinor Itzhak Zion Harush Beth Shemesh Engines Ltd. FAA & EASA Beth Shemesh Israel

In our study, stress-rupture tests were conducted at elevated temperatures to examine the impact of high temperature on marm247 LC (low carbon). Our main objective was to investigate the alterations in the microstructure, particularly the carbon precipitation, during long-term stress-rupture tests. It was observed that cracks developed near the sample neck, following the path of the carbides and the gamma matrix, rather than occurring in the gamma-gamma prime eutectic. This occurred despite the formation of carbides because of prolonged exposure to high temperature and load, and the crack propagation did not follow that path. Based on these findings, we suggest that a reduction in the carbon content of Mar-M247 LC can enhance the sample's lifespan when subjected to temperatures below 760˚C and a stress of 690 MPa.

关键词： marm247 Carbides Stress-Rupture High-Temperature Crack-Propagation

来源：

维普期刊数据库评论

在线全文

维普期刊数据库

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：