Effects of surface topography and specimen thickness on high-speed raindrop impact damage of CFRP laminates

Chinese Journal of Aeronautics 2023年第6期36卷 186-200页

作者： Naidan HOU Renxi ZHAO Xuan WANG Zhongbin TANG Hao CUI Yulong LI School of Aeronautics Northwestern Polytechnical UniversityXi'an 710072China Joint International Research Laboratory of Impact Dynamics and Engineering Application Xi'an 710072China Shaanxi Key Laboratory of Impact Dynamics and Engineering Application Xi'an 710072China School of Civil Aviation Northwestern Polytechnical UniversitySuzhou 215400China NPU Yangzi River Delta Research Institute Suzhou 215400China

Raindrop impact erosion has been observed since early days of aviation,and can be catastrophic for exposed materials during supersonic flight.A single impact waterjet apparatus is established for mimicking drop impacts at the velocities between 350 m/s and 620 m/*** Fiber Reinforced Polymer(CFRP)laminates with three different surface morphologies and specimen thicknesses are tested here.A central region with no visible damage has been noticed,surrounded by a"failure ring"with common damage patterns including resin removal,matrix cracking,fiber breakage and mass fiber *** features are presented in the"failure ring"whose whole scope extends larger along the longitudinal direction than the transverse direction of the top *** mechanism of the resin removal is related to fiber-matrix debonding,and its onset and propagation can be facilitated by initial surface asperities with the shear action of the lateral *** cases of multiple impact,good surface quality can slow down the evolution of resin removal and fiber exposure on the CFRP surface,reducing the erosion speed and delaying the occurrence of structural damages in the subsequent *** wave dominates the occurrence of matrix cracking on the CFRP surface,and subsequently,results in material loss and peeling of the top-layer because of lateral *** the increase of the specimen thickness,both the interlaminar and intralaminar failures decrease as the impact damage mechanism changes from plate bending stress to the reflection of stress waves.

关键词： Carbon fiber reinforced plastics Failure analysis Impact testing lateral jetting Surface roughness Waterjet

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：