Multiscale microstructural consideration of enhanced shear strength in TiAl intermetallic/K4169 alloy composite joints prepared by vacuum brazing with(Ti,Zr)-Ni-based amorphous filler metal

引用

Journal of Materials Science & Technology 2024年第5期172卷 51-70页

作者： Liangliang Zhang Honggang Dong Peng Li Baosheng Wu Yueting Ma Libing Huang Chao Li Jiachen Li School of Materials Science and Engineering Dalian University of TechnologyDalian 116024China

TiAl intermetallic could be used to replace Ni-based alloy in assemblies to generate excellent specific strength.A(Ti,Zr)-Ni-based amorphous filler metal Ti_(21.25)Zr_(25)Ni_(25)Cu_(18.75)(at.%)was designed using a cluster-plus-glue-atom model to successfully vacuum braze K4169 and TiAl bimetallic assemblies.At various brazing temperatures and holding time,the quantitative relationships between lattice distortion,grain boundary,dislocation density,and hardness,elastic modulus,shear strength of the joints were investigated.Meanwhile,the fracture mechanism of the joints was revealed.The brazed seam mainly consisted of solid diffusion reaction layers(ZonesⅠandⅢ)and filler metal residue zone(ZoneⅡ).When the brazing temperature increased to 1030℃,grain refinement occurred in the brazed seam.ZoneⅠwas primarily composed of(Ni)ss[0-11]+TiNi[011]/(Cr,Fe,Ni)ss[0-11]/(Ti,Zr)Ni[0-1-1]+(Cr,Fe,Ni)ss[0-11].The(Ti,Zr)(Ni,Cu)[001]and(Ti,Zr)(Ni,Cu)[101]intermetallic compound-based solid solutions were formed in ZoneⅡ.And the lattice distortion of(Ti,Zr)(Ni,Cu)[101]and(Ti,Zr)(Ni,Cu)[001]was 32.05%and 14.82%,respectively.As a result,the proportion of low angle grain boundaries(LAGBs)and deformed grains in ZoneⅡrose to 38.6%and 38.7%.In ZonesⅠandⅢ,the proportion of LAGBs reduced to 8%and 3.4%,respectively.As the holding time increased,the long-range diffusion of Al in ZoneⅡcaused the(Ti,Zr)(Ni,Cu)[001]with cubic structure to transform into(Ti,Zr)(Ni,Cu,Al)[00-1]with hexagonal crystal system structure,where the lattice distortion was 4.42%and 10.49%for a and c.At 1030℃/10 min,the average geometrically nec-essary dislocation densities(GNDs)in ZonesⅠ,ⅡandⅢwere 9.87×10^(14)m^(-2),8.55×10^(14)m^(-2)and 11.4×10^(14)m^(-2),respectively.Therefore,the shear strength of joints reached 322 MPa due to the lattice distortion,dislocation strengthening and fine grain strengthening.Meanwhile,the plastic and brittle hard phases were generated in ZoneⅡand displayed a mechanical interlocking structure that contributed to the performance of the joint.Bo

关键词： K4169/Ti_(21.25)Zr_(25)Ni_(25)Cu_(18.75)/TiAl composite joints intermetallic compound-based solid solution Lattice distortion Elastic modulus

来源：

维普期刊数据库评论

在线全文

维普期刊数据库

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：