Interfacial Oxides Evolution of High-Speed Steel Joints by hot-compression bonding

Acta Metallurgica Sinica(English Letters) 2022年第11期35卷 1837-1848页

作者： Wei-Feng Liu Bi-Jun Xie Ming-Yue Sun Bin Xu Yan-Fei Cao Dian-Zhong Li Shenyang National Laboratory for Materials Science Instituteof Metal ResearchChineseAcademyof SciencesShenyang 110016China School of Materials Scienceand Engineering University of Science and Technology of ChinaShenyang 110016China

The interfacial oxidation behavior of Cr_(4)Mo_(4) V high-speed steel(HSS)joints undergoing hot-compression bonding was investigated by using optical microscopy(OM),scanning electron microscopy(SEM),and transmission electron microscopy(TEM).In the heating and holding processes,dispersed rod-like and granularδ-Al_(2)O_(3) oxides were formed at the interface and in the matrix near the interface due to the selective oxidation and internal oxidation of Al,while irregular Si-Al-O compounds and spheroidal SiO_(2) particles were formed at the *** the post-holding treatment,SiO_(2) oxides and Si-Al-O compounds were dissolved into the matrix,andδ-Al_(2)O_(3) oxides were transformed into nanoscaleα-Al_(2)O_(3) particles,which did not deteriorate the mechanical properties of the *** formation and migration of newly-formed grain boundaries by plastic deformation and post-holding treatment were the main mechanism for interface *** tensile test results showed that the strength of the healed joints was comparable to that of the base material,and the in-situ tensile observations proved that the fracture was initiated at the grain boundary of the matrix rather than at the *** clarification of interfacial oxides and microstructure is essential for the application of hot-compression bonding of HSSs.

关键词： hot-compression bonding High-speed steel Interfacial oxides Interface healing Mechanical properties

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

Effects of Surface Roughness on Interface bonding Performance for 316H Stainless Steel in hot-compression bonding

引用

Acta Metallurgica Sinica(English Letters) 2023年第5期36卷 771-788页

作者： Yong Zhao Bi-Jun Xie Jin-Long Zhang Qin-Qiang Wang Bin Xu Jiang Guo Zhu-Ji Jin Ren-Ke Kang Dian-Zhong Li Key Laboratory for Precision and Non-Traditional Machining Technology of Ministry of Education Dalian University of TechnologyDalian116024China Shenyang National Laboratory for Materials Science Institute of Metal ResearchChinese Academy of SciencesShenyang110016China

The metallurgical bonding quality of bonding joints is affected by the substrate surface state in hot-compression bonding(HCB),and the surface roughness is a core indicator of the surface ***,the effects of surface roughness on interface bonding performance(IBP)in the HCB process are unclear for substrates with refractory oxide *** study presents the effects of surface roughness on IBP for 316H stainless steel joints fabricated by HCB.A set of HCB parameters for interface bonding critical state of 316H stainless steel joints was *** HCB experiments were carried out under parameters of interface bonding critical state to amplify the effect of surface *** interface morphologies,element distribution,and tensile properties were used to characterize the *** a result,the formation mechanisms of the interface pits were revealed and the variation trend of pit number with the roughness was ***,the mapping relation between surface roughness and IBP was *** results show that the degree of rotational dynamic recrystallization becomes weaker with the decrease in the surface roughness and the interface bonding mechanism is completely transformed into discontinuous dynamic recrystallization when the roughness is lower than 0.020μm *** number of interfacial pits decreases as the roughness decreases owing to the weakening of oxide scale aggregation and abrasive inclusion *** elongation of the tensile specimen cannot increase significantly while the roughness is lower than 0.698μm Sa.

关键词： Surface roughness Interface bonding performance hot-compression bonding Mapping relation Critical state

来源：

维普期刊数据库评论

在线全文

维普期刊数据库

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：