In Situ TiC/FeCrNiCu high-entropy alloy matrix composites:Reaction Mechanism,Microstructure and Mechanical Properties

引用

Acta Metallurgica Sinica(English Letters) 2020年第8期33卷 1091-1102页

作者： Hao Wu Si-Rui Huang Cheng-Yan Zhu Ji-Feng Zhang He-Guo Zhu Zong-Han Xie College of Materials Science and Engineering Nanjing University of Science and TechnologyNanjing 210094China School of Mechanical Engineering University of AdelaideSA 5005Australia School of Engineering Edith Cowan UniversityJoondalupWA 6027Australia

In situ TiC particles-reinforced FeCrNiCu high-entropy alloy matrix composites were prepared by vacuum induction melting *** reaction mechanisms of the mixed powder(Ti,Cu and C)were analyzed,and the mechanical properties of resultant composites were ***4Tiwere formed in the reaction of Cu and Ti when the temperature rose to 1160 *** the temperature further increased to 1182 K,newly formed Cu4Tireacted with C to give rise to TiC particles as reinforcement *** apparent activation energy for these two reactions was calculated to be 578.7 kJ/mol and 1443.2 kJ/mol,*** hardness,tensile yield strength and ultimate tensile strength of the 15 vol%TiC/FeCrNiCu composite are 797.3 HV,605.1 MPa and 769.2 MPa,respectively,representing an increase by 126.9%,65.9%and 36.0%as compared to the FeCrNiCu high-entropy base alloy at room ***,the elongation-to-failure is reduced from 21.5 to 6.1%with the formation of TiC *** was revealed that Orowan mechanism,dislocation strengthening and load-bearing effect are key factors responsible for a marked increase in the hardness and strength of the high-entropy alloy matrix composites.

关键词： high-entropy alloy matrix composite TiC particle Reaction mechanism Mechanical properties Strengthening mechanism

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：