high tap density of Ni_3(PO_4)_2 coated LiNi_(1/3)Co_(1/3)Mn_(1/3)O_2 with enhanced cycling performance at high cut-off voltage

引用

Chinese Journal of Chemical Engineering 2015年第1期23卷 315-320页

作者：崔妍徐盛明 Institute of Nuclear and New Energy Technology Tsinghua University

The Li Ni1/3Co1/3Mn1/3O2 is first obtained by the controlled crystallization method and then coated with Ni3(PO4)2particles. The effects of the coating on rate capability and cycle life at high cut-off voltage are investigated by electrochemical impedance spectroscopy and galvanostatic measurements. The element ratio of Ni:Mn:Co is tested by inductively-coupled plasma spectrometer(ICP) analysis and it testified to be 1:1:1. It is indicated that Ni3(PO4)2-coated Li Ni1/3Co1/3Mn1/3O2 has an outstanding capacity retention, where 99% capacity retention is maintained after 10 cycles at 5C discharge rate between 2.7 V and 4.6 V. The electrochemical impedance spectroscopy(EIS) results show that the current exchange density i0 of the coated sample is higher than that of Li Ni1/3Co1/3Mn1/3O2, which is beneficial to its electrochemical performances. All the conclusions show that the Ni3(PO4)2coating can prominently enhance the high rate performance of the Li Ni1/3Co1/3Mn1/3O2, especially at high cut-off voltage.

关键词： LiNi1/3Co1/3Mn1/3O2cathode material Electrochemistry Ni3(PO4)2coating high tap density high rate discharge capacity

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：