Enhanced cycling stability and rate performance of Co-doped and La_(2)O_(3)-coated LiNi_(0.9)Mn_(0.1)O_(2) toward power battery

引用

Rare Metals 2024年第2期43卷 658-670页

作者： Jia-Qi Peng Yuan-Yuan Wei Dong-Ming Liu Yun Li Bin Hu Bin Huang Jian-Wen Yang Shun-Hua Xiao Ren-Heng Wang Guangxi Key Laboratory of Electrochemical and Magneto-Chemical Functional materials College of Chemistry and BioengineeringGuilin University of TechnologyGuilin541004China Key Laboratory of Optoelectronic Devices and Systems of Ministry of Education and Guangdong Province College of Physics and Optoelectronic EngineeringShenzhen UniversityShenzhen518060China

Ultra-high nickel layered oxide cathode material with high energy density is the most promising material to improve the electrochemical performance of lithium-ion batteries(LIBs).However,the poor structural stability and severe surface/interface side reactions of the material lead to poor rate performance and cyclic stability,which limits its application in *** this paper,the dual-modification strategy of Co doping and La_(2)O_(3) coating is used to meet the above *** doping can effectively widen layer spacing and reduce Li^(+)/Ni^(2+) mixing,and La_(2)O_(3) coating can effectively eliminate the residual alkali on the surface of active material,inhibit the thickening of cathode electrolyte interphase(CEI)film and reduce surface/interface side ***,the modified material(NM90-CL)with excellent electrochemical properties is achieved through the synergistic enhancement of Co doping and La_(2)O_(3) *** capacity retention rate can reach 77.9%after 200 cycles at 1.0℃ and 75.7%after 200 cycles at 5.0℃.Its reversible capacity can up to 153.5 mAh·g^(–1) at 10.0℃.This dual-modification strategy will provide theoretical guidance and technical support for the synthesis of other high-performance electrode materials.

关键词： high nickel cathode material Co doping La_(2)O_(3) coating Electrochemical performance Electrochemical mechanism

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：