Improvement of Stress-rupture Life for Modified-hr6w Austenitic Stainless Steel

Journal of Materials Science & Technology 2011年第11期27卷 1059-1064页

作者： Shiyun Cui Zixing Zhang Yulai Xu Jun Li Xueshan Xiao Changchun Zhu Institute of Materials Shanghai University Shanghai 200072 China Baoshan Iron ＆ Steel Co. Ltd. Shanghai 200940 China

Stress-rupture life of hr6w austenitic stainless steel modified with B and Mg additions was measured, and the microstructures were analyzed by optical microscopy, X-ray diffraction, scanning electron microscopy and transmission electron microscopy equipped with energy dispersive spectroscopy The results indicated that the enhancement of the stress-rupture life was mainly due to the precipitation with B in the elemental form at the grain boundaries, and the improvement of the form of carbides at grain boundaries and the removal of O and S elements by addition of Mg. The micro-alloying elements have a beneficial effect on stress-rupture life of the modified-hr6w austenitic stainless steel at high temperature.

关键词： hr6w Micro-alloying Stress-rupture life Microstructure

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

高效超超临界机组用材hr3C和hr6w的热腐蚀行为及机理研究

引用

材料保护 2020年第7期53卷 154-161页

作者：鲍颖群苟远波梁志远浙江省特种设备科学研究院浙江杭州310020 西安航天动力研究所陕西西安710100 西安交通大学热流科学与工程教育部重点实验室陕西西安710049

为对比熔盐环境下典型耐热钢hr3C和铁镍基合金hr6w的热腐蚀行为及机理,在高温腐蚀试验系统上开展了750℃和810℃条件下1 000 h的熔盐腐蚀试验,利用扫描电镜、X射线衍射仪及能谱分析仪等表征了腐蚀产物成分与分布。结果表明:hr6w的腐蚀... 详细信息

为对比熔盐环境下典型耐热钢hr3C和铁镍基合金hr6w的热腐蚀行为及机理,在高温腐蚀试验系统上开展了750℃和810℃条件下1 000 h的熔盐腐蚀试验,利用扫描电镜、X射线衍射仪及能谱分析仪等表征了腐蚀产物成分与分布。结果表明:hr6w的腐蚀增重和腐蚀产物厚度均低于hr3C的;试验早期耐热材料的腐蚀主要受离子扩散控制,后期保护膜失效材料主要以失稳腐蚀为主。材料表面腐蚀产物主要为块状尖晶石结构和瘤状团聚物。产物主要为(Fe,Cr)2O3和Fe2O3,并有少量(Ni,Mn) Cr2O4。温度对于腐蚀过程的影响主要体现在提高反应离子活性与扩散速率,加速腐蚀的快速进行生成对应的腐蚀产物。模拟熔盐以熔融态盐膜形式沉积在耐热材料表面发生热腐蚀行为,且腐蚀层疏松多孔、层次分明,呈复合结构,即腐蚀外层为富Fe氧化物,腐蚀内层为富Cr氧化物,基体内侧出现明显内硫化区域。铁镍基合金hr6w的抗腐蚀性能优于耐热钢hr3C。

关键词：超超临界机组热腐蚀机理 hr3C hr6w 腐蚀产物熔盐

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

The Effect of Cold working on Creep Rupture Strength and Microstructure of Ni-23Cr-7w Alloy

引用

world Journal of Mechanics 2017年第10期7卷 283-295页

作者： Yoshiki Shioda Keiji Kubushiro Youhei Sakakibara Kyohei Nomura Yoshinori Murata Research Laboratory IHI Corporation Yokohama Japan Department of Materials Physics and Energy Engineering Nagoya University Nagoya Japan

In order to clarify the reason why the creep rupture time of pre-strained Ni-23Cr-7w Alloy (hr6w) is longer than that of the non-pre-strained hr6w, microstructures of hr6w after a series of creep tests were investigated. The creep tests were conducted at 750°C, 90 and 100 MPa. In the pre-strained samples, the grain boundary shielding ratio by precipitates was larger than that of the non-pre-strained sample. In addition, in the pre-strained samples the size of the M23C6 carbide in the grains was finer than in the non-pre-strained sample. The w content in the M23C6 carbide in the pre-strained samples tended to be larger than in the non-pre-strained sample. Therefore, the Ostwald ripening of the carbide was delayed and the size of M23C6 carbide was thought to be fine for a long time. These observations show that creep strength in the pre-strained samples is higher than that of the non-pre-strained sample because of both precipitation strengthening inside of the grains and grain boundaries.

关键词： A-USC hr6w Cold working Creep Strength Grain Boundary Shielding Ratio M23C6 Carbide

来源：

维普期刊数据库评论

在线全文

维普期刊数据库

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

在线全文

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

在线全文

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：