High-Temperature Fatigue Behavior of Inertia Friction Welded Joints of gh4065a Ni-Based Superalloy

Acta Metallurgica Sinica(English Letters) 2024年第11期37卷 1935-1946页

作者： Xiaoguang Li Jiatao Liu Qing Liu Chunbo Zhang Hang Liang Lei Cui Yongchang Liu School of Materials Science and Engineering Tianjin UniversityTianjin300072China AECC Shenyang Liming Aero-Engine Co. LtdShenyang110043China Harbin Welding Institute Co. LtdHarbin150028China Tianjin Key Laboratory of Advanced Joining Technology Tianjin300072China

In this work,the novel Ni-based superalloy gh4065a inertia friction welding(IFW)joints were subjected to the post-welding heat treatments(PWHT)at 730℃for 5 h or 760℃for 5 h,and the differences in microstructure characteristics,local mechanical properties,and fatigue failure life were ***,based on the high-temperature low-cycle fatigue testing and characterization results,the correlation between the microstructure characteristics and low-cycle fatigue damage behavior was systematically *** was found that there were smaller grains in the thermo-mechanically affected zone(TMAZ)than in the weld zone and heat-affected zone(HAZ),and the boundary region between TMAZ and HAZ was the fatigue failure position of IFW joints under the high-temperature low-cycle fatigue *** fatigue testing results showed that the high-temperature fatigue performance for gh4065a IFW joints degenerated with the increase in PWHT *** existed cyclic softening and inhomogeneous fatigue damage in an IFW joint,which was more significant under the 760℃5 h PWHT ***,dislocation tangles and cells formed in the boundary region between TMAZ and HAZ under the fatigue *** difference in grain size after the IFW process and the inhomogeneousγ′phrase re-precipitation after the PWHT in the boundary region between TMAZ and HAZ resulted in the local inhomogeneous strengthening,corresponding to uneven plastic deformation and fatigue failure behavior under the fatigue loadings.

关键词： Inertia friction welding gh4065a alloy Low-cycle fatigue Post-welding heat treatment Fatigue behavior

来源：

维普期刊数据库评论

在线全文

维普期刊数据库

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：