Mechanical Property of M40J_f/5A06Al Composite at Elevated Temperatures

Acta Metallurgica Sinica(English Letters) 2015年第9期28卷 1175-1182页

作者： Da-Guang Li Guo-Qin Chen Long-Tao Jiang Xiu Lin Gao-Hui Wu School of Materials Science and Engineering Harbin Institute of Technology State Key Laboratory of Advanced Welding and Joining Harbin Institute of Technology Heilongjiang Academy of Industrial Technology

In this work, aluminum alloy with a high concentration of magnesium （5A06） was reinforced with 55 vol% unidirectional ultra-high modulus and highly graphitized carbon fiber （M40J） using pressure infiltration method. The effect of temperature on the bending strength of the Cf/A1 composites was investigated from room temperature to 500 ℃. The experimental results showed that the strength of M40Jf/5A06A1 composites was not affected by temperature from room temperature to 200 ℃. The bending strength of the composite at 300 ℃ was decreased by 30% compared with that at room temperature. In order to evaluate the extent of interface weakening, the length of fiber pullout was measured. The results showed that the pullout length reached the maximum at 300 and 500 ℃, which indicated weak interface at the corre- sponding temperature. The DSC curve presented obvious heat absorption peak at around 300 ℃, which may be attributed to the dissolution of the interfacial product （A13Mg2） phases at the C/A1 interface. The bending fracture surfaces of the composites after three-point bending tests were observed by SEM, plastic-viscous flow of the matrix were observed at the samples tested at 500 ℃. The predominant mechanisms for high-temperature damage of M40Jf/5A06A1 composites are matrix softening caused by dislocation recovery and interface weakening caused by the dissolution of interfacial products.

关键词： Carbon fiber Aluminum Metal matrix composites High-temperature properties fiberpullout length

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：