Microstructure and mechanical properties in the TLP joint of feconitial and Inconel 718 alloys using BNi2 filler

Journal of Materials Science & Technology 2021年第2期61卷 176-185页

作者： Lin Yuan Jiangtao Xiong Yajie Du Jin Ren Junmiao Shi Jinglong Li State Key Laboratory of Solidification Processing Northwestern Polytechnical UniversityXi'an 710072China Shaanxi Key Laboratory of Friction Welding Technologies Northwestern Polytechnical UniversityXi'an 710072China

High entropy alloy(HEA) of Fe Co Ni Ti Al and Inconel 718 superalloy were firstly transient liquid phase(TLP) bonded by BNi2 filler due to the diffusion of Si and B in the filler to the base metals. The effects of bonding time on microstructure evolution and mechanical properties of the TLP joints were *** to the complete isothermal solidification of the joints bonded for 30 min 120 min at 1100°C,no athermally solidified zones(ASZs) formed by eutectic phases were observed in the welded zone. Thus the TLP joints were only composed by the isothermally solidified zone(ISZ) and two diffusion affected zone(DAZ) adjacent to the dissimilar base metals and the negative effect of the ASZ on joint properties can be avoided. In addition, the increase of the bonding time can also make the Ti B2 borides precipitated in the DAZ near HEA and the brittle borides or carbides in the DAZ near IN718 alloy decrease and reduce the possibility of the stress concentration happened in the joints under loading. Therefore, the highest shear strength(632.1 MPa) of the TLP joints was obtained at 1100°C for 120 min, which was higher than that of the joint bonded for 30 min, 404.2 MPa. Furthermore, the extension of the bonding time made the fracture mechanism of the joint be transformed from the intergranular fracture to the transgranular fracture. However, as the brittle borides in the DAZ near IN718 can not be eliminated completely and refining of grains also happened in such region, all the TLP joints fractured inner the DAZ near IN718 alloy.

关键词： feconitial alloy Inconel 718 alloy Microstructure evolution Mechanical properties Fracture mechanism

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：