deformation Behavior of fe-36ni steel during cryogenic( 123-173 K) rolling

Journal of Iron and steel Research(International) 2016年第5期23卷 447-452页

作者： Jian-jun ZHENG Chang-sheng LI Shuai HE Ban CAI Yan-lei SONG State Key Laboratory of rolling and Automation Northeastern University

Microstructural evolution and mechanical properties of cryogenic rolled fe-36ni steel were investigated. The annealed fe-36ni steel was rolled at cryogenic temperature（ 123-173 K） with 20%- 90% rolling reduction in thickness.The deformation process was accompanied by twinning at cryogenic temperature,and the mean thickness of deformation twins was about 200 nm with 20% rolling reduction. When the rolling reduction was above 40%,twinning was suppressed due to the stress concentration in the tested steel. deformation microstructure of fe-36ni steel consisted of both twin boundaries and dislocations by cryogenic rolling（ CR）,while it only contained dislocations after rolling at room temperature（ RT）. The tensile strength of fe-36ni steel was improved to 930 MPa after 90% reduction at cryogenic temperature,while the tensile strength after 90% reduction at RT was only 760 MPa. More dislocations could be produced as the nucleation sites of recrystallization during CR process.

关键词： fe-36ni steel cryogenic rolling twinning dislocation slip room temperature deformation microstructure

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：