Effects of Mechanical Milling and sintering Temperature on the Densification, Microstructure and Tensile Properties of the fe–mn–si Powder Compacts

引用

Journal of Materials Science & Technology 2016年第11期32卷 1161-1170页

作者： Zhigang Xu Michael A.Hodgson Peng Cao Department of Chemical and Materials Engineering University of Auckland Private Bag 92019 Auckland 1142 New Zealand

This work reported on the effects of mechanical milling and sintering temperature on the densification,microstructure and mechanical properties of the fe–28mn–3si（wt%） alloy. Elemental fe, mn and si powders were used as the starting materials, and two batches of powder mixture were prepared： one was blended elemental（BE） powder mixture; the other was mechanically milled（MM） powder mixture milled for5 h using planetary ball milling. Both powder mixtures were pressed under a uniaxial pressure of 400 MPa,and subsequently sintered in a high vacuum furnace for 3 h at 1000, 1100, 1200 and 1300 °C. It was found that mn depletion region（MDR） was formed on the surface of all the sintered samples. The sintered BE compacts had a low density（〈68.2%） at all temperatures, while the density of the sintered MM compacts increased drastically from ~65% at 1000 °C to ~91% at 1300 °C. All the sintered MM compacts were composed of a predominant γ-austenite and minor ε-martensite. In comparison, additional（fe, mn）3si phase was observed in the BE alloys sintered at 1000 °C, and a single α-fe phase was identified in the BE compact sintered at 1300 °C. The tensile properties of the sintered MM compacts increased significantly with the temperature and were significantly higher than those of their BE counterparts.

关键词： fe–mn–si alloys Vacuum sintering Density Microstructure Tensile properties

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：