材料工程 2017年第5期45卷 31-37页

作者：刘天娇陈惠鹏张卫方娄伟涛北京航空航天大学可靠性与环境工程技术国防科技重点实验室北京100191

B10铜镍合金具有优良的耐海水腐蚀性能,为研究其在海水中的腐蚀行为,取厦门天然海水,加入双氧水作为腐蚀加速剂,在室内模拟海水全浸腐蚀实验,采用失重法、电化学阻抗谱(EIS)技术分析B10合金在海水腐蚀中的腐蚀速率随腐蚀时间的变化规律... 详细信息

B10铜镍合金具有优良的耐海水腐蚀性能,为研究其在海水中的腐蚀行为,取厦门天然海水,加入双氧水作为腐蚀加速剂,在室内模拟海水全浸腐蚀实验,采用失重法、电化学阻抗谱(EIS)技术分析B10合金在海水腐蚀中的腐蚀速率随腐蚀时间的变化规律,用不同腐蚀周期的电化学阻抗谱特征来表征工作面积为1cm^2的合金表面氧化膜的生长破坏情况。结合扫描电子显微镜(SEM)、能谱分析(EDX)、XPS和拉曼光谱技术分析B10合金表面腐蚀产物膜的成分以及B10合金在海水腐蚀中的腐蚀类型。结果表明,氧化膜的生成与破坏使得合金在海水中的瞬态腐蚀速率呈先减小后增大的趋势,腐蚀产物包含碱式氯化铜Cu_2(OH)_3Cl和氧化亚铜Cu_2O,腐蚀由点蚀开始,逐渐经历了晶间腐蚀-剥蚀。

关键词： B10铜镍合金, 海水腐蚀, EIS, SEM, 腐蚀产物

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

LiCoO_2 electrode/electrolyte interface of Li-ion batteries investigated by electrochemical impedance spectroscopy

引用

Science China Chemistry 2007年第6期50卷 776-783页

作者： ZHUANG QuanChao1, 2, XU JinMei1, FAN XiaoYong1, WEI GuoZhen1, DONG QuanFeng1 JIANG YanXia1, HUANG Ling1 & SUN Shigang1 1 State Key Lab of Physical Chemistry of Solid Surfaces, Department of Chemistry, Xiamen University, Xiamen 361005, China 2 School of Materials Science and Engineering, China University of Mining & Technology, Xuzhou 221116, China State Key Lab of Physical Chemistry of Solid Surfaces Department of ChemistryXiamen UniversityXiamen 361005China School of Materials Science and Engineering China University of Mining & TechnologyXuzhou 221116China

The storage behavior and the first delithiation of LiCoO2 electrode in 1 mol/L LiPF6-EC:DMC:DEC elec- trolyte were investigated by electrochemical impedance spectroscopy (EIS). It has found that, along with the increase of storage time, the thickness of SEI film increases, and some organic carbonate lithium compounds are formed due to spontaneous reactions occurring between the LiCoO2 electrode and the electrolyte. When electrode potential is changed from 3.8 to 3.95 V, the reversible breakdown of the resistive SEI film occurs, which is attributed to the reversible dissolution of the SEI film component. With the increase of electrode potential, the thickness of SEI film increases rapidly above 4.2 V, due to overcharge reactions. The inductive loop observed in impedance spectra of the LiCoO2 electrode in Li/LiCoO2 cells is attributed to the formation of a Li1-xCoO2/LiCoO2 concentration cell. Moreover, it has been demonstrated that the lithium-ion insertion-deinsertion in LiCoO2 hosts can be well described by both Langmuir and Frumkin insertion isotherms, and the symmetry factor of charge transfer has been evaluated at 0.5.

关键词： Li-ion batteries, LiCoO2, EIS, SEI film, inductance

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：