Influence of dc current on Corrosion Behaviour of Copper–Aluminium Composite Plates

Acta Metallurgica Sinica(English Letters) 2021年第8期34卷 1142-1152页

作者： Yu-Lin Cheng Xiao-Jiao Zuo Xiao-Guang Yuan Hong-Jun Huang Yi-Fan Zhang School of Materials Science and Engineering Shenyang University of TechnologyShenyang 110870China

In this study, neutral salt spray accelerated corrosion test of copper–aluminium composite under 0–125 A dc current was carried out under 5% concentration. The effect of corrosion behaviour on copper–aluminium composite by dc current was carried out by a scanning electron microscope(SEM) with energy-dispersive spectroscopy(EDS), X-ray diffraction(XRD) patterns, X-ray photoelectron spectroscopy(XPS), weight-loss method and electrochemical analysis. The results show that the current can accelerate the corrosion rate. Meanwhile, the current temperature effect can reduce the corrosion rate. The current caused directional migration of ions resulting in different corrosion products on positive and negative poles of specimen, and the corrosion degree on the positive pole was more serious. The galvanic corrosion mechanism at the copper–aluminium interface is different from the pitting corrosion mechanism far away from the interface, and the latter is more affected by dc current.

关键词： Copper–aluminium composite Corrosion dc current Ionic migration Temperature effect

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：