Brazing of WC–8Co cemented carbide to steel using cu–ni–al alloys as filler metal: Microstructures and joint mechanical behavior

引用

Journal of Materials Science & Technology 2018年第7期34卷 1180-1188页

作者： Xiangzhao Zhang Guiwu Liu Junnan Tao Yajie Guo Jingjing Wang Guanjun Qiao School of Materials Science and Engineering Jiangsu University Engineering Research Center of Transportation Materials of Ministry of Education School of Materials Science and Engineering Chang'an University School of Materials Science and Engineering Shanghai University State Key Laboratory for Mechanical Behavior of Materials Xi'an Jiaotong University

Three novel cu-ni-A1 brazing filler alloys with cu/ni weight ratio of 4：1 and 2.5-10 wt% al were developed and characterized, and the wetting of three cu-ni-al alloys on WC-8Co cemented carbide were investigated at 1190-1210 ℃ by the sessile drop technique. Vacuum brazing of the WC-8Co cemented carbide to SAE1045 steel using the three cu-ni-al alloys as filler metal was further carried out based on the wetting test results. The interfacial interactions and joint mechanical behaviors involving microhardness, shear strength and fracture were analyzed and discussed. The experimental results show that all the three wetting systems present excellent wettability with final contact angles of less than 5 °and fast spreading. An obvious degeneration layer with continuous thin strip forms in the cemented carbide adjacent to the cu-ni-A1/WC-8Co interface. The variation of microhardness in the joint cross-section is closely related to the interactions （such as diffusion and solid solution） of WC-8Co/cu-ni-al/steel sys- tem. Compared with the other two brazed joints, the WC-8Co/cu-19ni-Sal/steel brazed joint presents more reliable interlayer microstructure and mechanical property while brazing at the corresponding wetting temperatures for 5 rain, and its average shear strength is over 200 MPa after further optimizing the brazing temperature and holding time. The joint shear fracture path passes along the degeneration layer, cu-ni-A1/WC-8Co interface and brazing interlayer, showing a mixed ductile-brittle fracture.2018 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science ＆ Technology.

关键词： cu-ni-al alloy Cemented carbide Brazing Microstructures Mechanical properties

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：