Significant annealing-induced hardening effect in nanolaminate d-nanotwinne d(crconi)_(97.4)Al_(0.8)Ti_(1.8)me dium-entropy alloy by severe cold rolling

引用

Journal of Materials Science & Technology 2024年第3期170卷 156-166页

作者： Shuqing Yuan Hui Fu Lei Qian Chi Fai Cheung Xu-Sheng Yang State Key Laboratory of Ultra-precision Machining Technology Department of Industrial and Systems EngineeringThe Hong Kong Polytechnic UniversityHung HomKowloonHong KongChina Hong Kong Polytechnic University Shenzhen Research Institute Shenzhen 518060China

Due to the easy coarsening caused by poor thermal stability,the verified annealing-induced hardening in nanograined metals can only maintain at a relatively low-temperature range.In this study,a nanolam-inated(crconi)_(97.4)Al_(0.8)Ti_(1.8)medium-entropy alloy with an average lamellae thickness of∼20 nm embedded by thinner nanotwins was fabricated by severe cold rolling to achieve superior thermal stability.Compared with the conventional nanotwinned crconi with nanotwins inside ultra-fined grains,the hier-archical nanolaminated-nanotwinned(crconi)_(97.4)Al_(0.8)Ti_(1.8) exhibits a significant annealing-induced hard-ening effect,i.e.,hardness increasing from∼250 HV in the original specimen to∼500 HV in the cold-rolled status and finally∼630 HV after annealing at 600℃for 1 h.Detailed microstructure characterizations reveal that the reduced dislocation density and formation of L1_(2)ordered domain are mainly responsible for such hardening effect,which is facilitated by the effectively suppressed coarsening with annealing temperature,i.e.,slow detwinning process and well-retained low-angle nanolamellar structure.The coarsening mechanisms from the cold-rolled nanolamellae to the fully recrystallized micro-equiaxed structures under the annealing temperatures ranging from 400 to 800℃ were also elucidated by atomic observations.

关键词： Annealing-induced hardening Thermal stability Nanolaminated-nanotwinned structure crconi detwinning Grain boundary migration

来源：

维普期刊数据库评论

在线全文

维普期刊数据库

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：