Effect of alumina content and heat treatment on microstructure and upconversion emission of Er^(3+)ions in oxyfluoride glass-ceramics

引用

Journal of Rare Earths 2012年第12期30卷 1228-1234页

作者： Mohammad Hasan Imanieh Bijan Eftekhari Yekta Vahak Marghussian Inocencio Rafael Martin Benenzuela Alberto Hernandez Creus Saeed Shakhesi Esmaeil Eslami Department of Materials Ceramic DivisionIran University of Science and Technology Nanotechnology Department Engineering Research Institute Department of Física Fundamental Electrónicay SistemasUniversity of La LagunaC.Astrofísico Francisco Sánchezs/n E-38206 La LagunaTenerifeSpain MALTA Consolider Team University of La LagunaC.Astrofísico Francisco Sánchezs/n E-38206 La LagunaTenerifeSpain Department of Química Física Instituto de Materialesy NanotecnologíaUniversity of La Laguna38205-La LagunaTenerifeSpain Nanotechnology Department Engineering Research Institute Tehran Department of Physics Iran University of Science and Technology (IUST)NarmakTehranIran

The effect of alumina content and heat treatment temperature and time, on microstructure and Er3＋（0.5 mol.%） emission of oxyfluoride glass-ceramics were investigated in this research. Two values of 1.8 （SA1.8Er0.5） and 2.18 （SA2.18Er0.5） were selected in this research for SiO2/Al2O3 ratio. According to DTA results, precursor glasses were heat treated at 630, 660 and 690 ℃ for 4 h and some glasses were also heat treated at 630 ℃ for 48 and 72 h. The results indicated that alumina content had significant effect on phase separation and viscosity of the glasses. Therefore the size, size distribution, and volume concentration of nano caf2 crystals which precipitated during the heat treatment depended on alumina content of the glass. Due to the much smaller size of the precipitated caf2 crystals in the glasses of low alumina content, these samples maintained excellent transparency and had narrower crystal size distribution than the high alumina glasses. The crystal size was increased markedly with the temperature increasing from 630 to 690 ℃. On the other hand a slight increase was observed in the crystal size by raising the heat treatment time in both glasses. Results indicated that in low alumina content glass （SA2.18Er0.5） the size of caf2 nanocrystals was controlled in one order of magnitude. The increase of heat treatment time and temperature led to the incorporation of Er3＋ ions into caf2 crystalline phase, increasing significantly the upconversion intensity. After heat treatment at 690 ℃for 4 h, atomic force microscope （AFM） revealed the development of small crystals with an average size of 80 and 30 nm in SA1.8Er0.5 and SA2.18Er0.5 samples, respectively.

关键词： oxyfluorides glass-ceramic caf2 nanocrystals SiO3/Al2O3 ratio rare earths

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：