Fabrication of AI foam without thickening process through melt-foaming method

Journal of Iron and Steel Research(International) 2018年第1期25卷 90-98页

作者： Dong-hui Yang Jian-qing Chen Lei Wang Jing-hua Jiang Ai-bin Ma College of Mechanics and Materials Hohai UniversityNanjing 210098 Jiangsu China Suqian Research Institute of Hohai University Suqian 223814 Jiangsu China

By using calcium carbonate （CaCO3） powder as the blowing agent, Al foams with porosities of - 60 to 85% and pore size of - 1.5 mm were fabricated via melt-foaming method. Instead of adding a thickening agent to increase Al melt viscosity, a small amount of Mg ingot （5.0 wt%） was added first, and then A1 melt was foamed by adding calcium carbonate via the impellor stirring. The effect of Mg addition on the gas release behavior of calcium carbonate in the Al melt was investigated. The compression behavior of fabricated Al foams was examined. The results show that the blowing gas is possibly from the reaction between Mg and calcium carbonate, and this reaction can produce solid oxides with micrometer level size, which leads to increasing the Al melt viscosity and is beneficial for inhibiting pores coarsening. Besides, the micrometer level cracks in the cell walls make the strength of Al foam decrease.

关键词： Al foam Thickening agent Calcium carbonate blowing gas Compression

来源：

维普期刊数据库评论

在线全文

维普期刊数据库

学校读者我要写书评

暂无评论

Mg Alloy Foam Fabrication via Melt Foaming Method

引用

Journal of Materials Science & Technology 2008年第3期24卷 302-304页

作者： Changhwan SEO Bo-Young HUR i-Cube Center ERISchool of Nano & Advanced Materials EngineeringGyeongsang National University

For the first time AZ91 （MgAl9Zn1） and AM60 （MgAl6） Mg alloy foams with homogeneous pore structures were prepared successfully via melt foaming method using CaCO3 as blowing agent. It is revealed that the blowing gas to foam the melt is not CO2 but CO, which comes from liquid-solid reaction between Mg melt. The reaction temperature is more than 100℃ lower than CaCO3 decomposition, which makes Mg alloy melts foam into cellular structure much more easily in the temperature range from 690℃ to 750℃.

关键词： Mg alloy foam CaCO3 blowing gas

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：