Influence of austempering process on microstructures and mechanical properties of V-containing alloyed ductile iron

Journal of iron and Steel Research International 2018年第1期25卷 81-89页

作者： Jun-jun Cui Li-qing Chen State Key Laboratory of Rolling and Automation Northeastern University Shenyang 110819 Liaoning China College of Mechanical and Vehicle Engineering ShenyangInstitute of Technology Fushun 113122 Liaoning China

The influence of austempering time and vanadium addition on microstructure and mechanical properties of the alloyed ductile iron has been investigated. The 0.30 wt% V-containing and V-free alloyed ductile irons were firstly austenitized at 850 ℃ for 1 h and then austempered in a salt bath at 300 ℃ for 2, 3 and 4 h, respectively. For the 0.3 wt% V-containing alloyed ductile iron, the transformation product （ausferrite） was finer, and a small amount of martensite and a large amount of stable austenite were obtained after austempering for 2 h, while higher hardness and compressive strength of 62.8 HRC and 3000 MPa were achieved. For the V-free alloyed ductile iron, lower hardness and compressive strength were measured to be 56.8 HRC and 2320 MPa. As the austempering time increases, the amount of stable austenite decreases in the V-containing ductile iron, typically for the start of the second stage formation （retained austenite （γτ） →α ＋ carbide）. Based on this, it is assumed that the optimal processing window （OPW） was narrowed due to the addition of 0.30 wt% V as compared to the V-free ductile iron. When the hardness of 0.30 wt% V-alloyed ductile iron was higher than 59 HRC, the highest wear resist- ance was obtained. The mechanical cutting plays a dominant role in abrasive wear process.

关键词： alloyed ductile iron Vanadium Austempering Microstructure Property Wear resistance

来源：

维普期刊数据库评论

在线全文

维普期刊数据库

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：