Fabrication and characterization of GNPs and CNTs reinforced al7075 matrix composites through the stir casting process

引用

International Journal of Minerals,Metallurgy and Materials 2021年第7期28卷 1204-1214页

作者： Siavash Imanian Ghazanlou Beitallah Eghbali Faculty of Materials Engineering Sahand University of TechnologyTabriz 51335-1996Iran

This study investigated the effects of adding graphene nanoplates(GNPs)and carbon nanotubes(CNTs)into the al7075 matrix via the stir casting method on the microstructure and mechanical properties of the fabricated composites.By increasing the volume fraction of rein-forcements,the fraction of porosity increased.The X-ray diffraction results showed that the addition of reinforcements into the al7075 changed the dominant crystal orientation from(002)to(111).Field emission scanning electron microscopy images also showed the distribution of clustered reinforcements in the matrix.Between the two reinforcements,the addition of CNTs generated a lower fraction of porosities.Through the addition of 0.52vol%GNPs into the matrix,the hardness,ultimate tensile strength and uniform elongation increased by 44%,32%,and 180%,respectively.Meanwhile,the presence of 0.71vol%CNTs in the matrix increased the hardness,tensile strength and uniform elongation by 108%,129%,and 260%,respectively.

关键词： al7075 GNPs CNTs stir casting composite

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

Finite Element Study on the Development of Damage and Flow Characteristics in al7075 alloy during Ex-ECAP

引用

Modeling and Numerical Simulation of Material Science 2013年第1期3卷 27-32页

作者： Mehdi Shaban Ghazani Beitallah Eghbali Department of Materials Engineering Sahand University of Technology Tabriz Iran

In the present study, 3D-finite element method was conducted to investigate the deformation characteristics of al7075 alloy during integrated extrusion-equal channel angular pressing. Effective strain, strain rate, mean stress, and damage distributions were evaluated. Severe cracking was observed at al7075 sample after extrusion-equal channel angular pressing. Finite element results show that cracking is due to the positive mean stress and damage accumulation at the top surface of sample.

关键词： Finite Element Method Extrusion Equal Channel Angular Pressing al7075

来源：

维普期刊数据库评论

在线全文

维普期刊数据库

学校读者我要写书评

暂无评论

Corrosion Behavior of Cenosphere Reinforced al7075 Metal Matrix Composite —An Experimental Approach

引用

Journal of Minerals and Materials Characterization and Engineering 2018年第3期6卷 424-437页

作者： Ravi Kumar D. V. Seenappa C. R. Prakash Rao V. Bharat Department of Mechanical Engineering Global Academy of Technology Bengaluru India Department of Mechanical Engineering Government Engineering College Ramanagara India

aluminum-based metal matrix composites (MMCs) are considered in several technological applications owing to their enhanced mechanical properties when compared with monolithic metals. Research on the mechanical properties MMCs was done by many researchers;however in depth study on the oxidation behavior of cenosphere, reinforced MMCs are required, since the application of aluminum-based MMCs is extensively used in applications like automobile, navigation and aviation, where the demand on light weight corrosion resistance material is very much required. In the present work varied compositions of al7075 grade aluminum-cenosphere composites use liquid metallurgy route adopting stir casting approach. The experimental study was aimed at experimental investigations of developed composites under different corrosive environments. The corrosion tests were carried out as per ASTM standards. Salt spray test using NaCl was carried out as per ASTM B117 and immersion tests using NaCl and NaOH as corrodents were carried out by following ASTM G31 standards. The results obtained from the tests revealed that as increase in weight % of reinforcement, corrosion resistance increases up to 7.5% reinforcement, and further the corrosion resistance decreases marginally. Solution heat treated samples exhibited higher resistance to oxidation than cast samples in all corrosive environments. The SEM images show the presence of micro cracks and occurrence of pitting corrosion on the corrosion tested specimens.

关键词： al7075 Cenosphere Metal Matrix Composites NaCl NaOH Salt Spray Test Corrosion Wear

来源：

维普期刊数据库评论

在线全文

维普期刊数据库

学校读者我要写书评

暂无评论

钝圆半径对径向中径差影响的数学模型分析

引用

机床与液压 2022年第24期50卷 114-120页

作者：任杰李婷婷孟宇张锐闫献国太原科技大学机械工程学院山西太原030024 太原铁路机械学校山西太原030006 山西医科大学药学院山西太原030001

螺纹连接作为飞机中最重要承力构件,对飞机的安全性有重大的影响。所以在制造飞机的常用材料al7075上制造出高质量的内螺纹就显得十分关键。径向中径差作为评价内螺纹质量的重要参数,对内螺纹的质量影响很大。钝圆半径会影响内螺纹的加... 详细信息

螺纹连接作为飞机中最重要承力构件,对飞机的安全性有重大的影响。所以在制造飞机的常用材料al7075上制造出高质量的内螺纹就显得十分关键。径向中径差作为评价内螺纹质量的重要参数,对内螺纹的质量影响很大。钝圆半径会影响内螺纹的加工质量,为了研究它对al7075攻丝加工的径向中径差影响,建立攻丝加工的准静态数学模型来进行仿真,并通过试验进行验证。结果表明:模型能够有效预测径向中径差的变化趋势;径向中径差随钝圆半径的增加呈先减小后增大的趋势,并且在10μm时获得了最小的径向中径差。

关键词：径向中径差钝圆半径 al7075 攻丝加工

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

磁粒研磨去除al 7075交叉孔棱边毛刺的试验研究

引用

表面技术 2019年第4期48卷 302-309页

作者：焦安源张龙龙刘新龙陈燕辽宁科技大学辽宁鞍山114051

目的探究磁粒研磨法对去除al7075交叉孔棱边毛刺的影响,提高孔道的研磨质量及毛刺去除效率。方法首先,通过对圆柱型磁极进行轴向、径向开槽,并利用ANSOFT软件对磁极进行磁场模拟,分析三种不同形状的磁极的磁感应强度变化;其次,通过磁粒... 详细信息

目的探究磁粒研磨法对去除al7075交叉孔棱边毛刺的影响,提高孔道的研磨质量及毛刺去除效率。方法首先,通过对圆柱型磁极进行轴向、径向开槽,并利用ANSOFT软件对磁极进行磁场模拟,分析三种不同形状的磁极的磁感应强度变化;其次,通过磁粒研磨法对交叉孔孔道内壁进行研磨,去除棱边毛刺;最后,测取交叉孔表面微观形貌、材料去除量、毛刺高度和表面粗糙度。结果研磨加工时间为10 min、磁极转速为1500 r/min的条件下,磁极为径向开槽时,材料去除量高达46 mg,孔道内壁的表面粗糙度由原始1.5μm降至0.5μm,孔道表面研磨效果较为理想,棱边毛刺完全去除;当磁极为非开槽时,材料去除量为40 mg,表面粗糙度下降至0.65μm,棱边毛刺几乎完全去除;磁极为轴向开槽时,表面粗糙度下降至0.8μm左右,材料去除量约为30 mg,剩余毛刺高度约为5μm。结论研磨时间为10 min,磁极转速为1500 r/min,当磁极径向开槽时,相对于轴向开槽磁极和不开槽磁极,磁粒研磨al7075交叉孔内表面的效果更好,毛刺去除效率更高。

关键词：磁粒研磨 al7075 交叉孔毛刺表面形貌粗糙度

来源：

维普期刊数据库

同方期刊数据库评论

在线全文

学校读者我要写书评

暂无评论

欢迎您,

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

在线全文

在线全文

在线全文

在线全文

请选择保存的检索档案：

请选择收藏分类：

通借通还

欢迎您,

建议与咨询 留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

时间限定

文献类型

馆藏选择

核心期刊

语言

文献类型

帮助

文字说明：

检索规则说明：

检索范例：

分类表

所选分类

限定检索结果

文献类型

馆藏范围

日期分布

学科分类号

主题

机构

作者

语言

在线全文

在线全文

在线全文

在线全文

在线全文

请选择保存的检索档案： 新增检索档案 确定 取消

请选择收藏分类： 新增自定义分类 确定 取消

通借通还

建议与咨询留下您的常用邮箱和电话号码，以便我们向您反馈解决方案和替代方法

请选择保存的检索档案：

请选择收藏分类：